Design of Small Stone Asphalt Mixture based on Anti-skidding Performance

来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2012年第4期

论文作者:李蕊 裴建中

文章页码:789 - 793

摘    要:Small stone asphalt mixture(SSAM) was designed by Bailey method and coarse aggregate voids-filling method.The optimum asphalt content was determined by Marshal test.Surface texture depth for SSAM with different voidage,and the BPN of SSAM and SMA before after wet track abrasion were measured.The experimental results indicate that the surface texture depth increases with the decreasing of asphalt aggregate ratio.The SSAM with the optimal asphalt content has a good skid resistance.BPN of asphalt mixture decreases with the increasing of wearing time,but the extent of reduction is different.The reduction rate of BPN for SSAM is smaller than that of SMA,indicating that SSAM has a good skid resistance attenuation capacity.Finally,the other properties of SSAM are also evaluated,showing that the splitting strength and modulus and SSAM are higher than those of SMA,and the other properties of SSAM,such as high-temperature performance and water stability can also satisfy the technical requirements.

详情信息展示

Design of Small Stone Asphalt Mixture based on Anti-skidding Performance

李蕊,裴建中

Key Laboratory for Special Area Highway Engineering of Ministry of Education,Chang’an University

摘 要:Small stone asphalt mixture(SSAM) was designed by Bailey method and coarse aggregate voids-filling method.The optimum asphalt content was determined by Marshal test.Surface texture depth for SSAM with different voidage,and the BPN of SSAM and SMA before after wet track abrasion were measured.The experimental results indicate that the surface texture depth increases with the decreasing of asphalt aggregate ratio.The SSAM with the optimal asphalt content has a good skid resistance.BPN of asphalt mixture decreases with the increasing of wearing time,but the extent of reduction is different.The reduction rate of BPN for SSAM is smaller than that of SMA,indicating that SSAM has a good skid resistance attenuation capacity.Finally,the other properties of SSAM are also evaluated,showing that the splitting strength and modulus and SSAM are higher than those of SMA,and the other properties of SSAM,such as high-temperature performance and water stability can also satisfy the technical requirements.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号