A study on hydrogen storage and electrochemical properties of La0.55Pr0.05Nd0.15Mg0.25Ni3.5 (Co0.5Al0.5)x (x=0.0, 0.1, 0.3, 0.5) alloys

来源期刊:JOURNAL OF RARE EARTHS2012年第3期

论文作者:覃铭 蓝志强 丁杨 熊凯 刘奕新 郭进

文章页码:222 - 227

摘    要:The La0.55Pr0.05Nd0.15Mg0.25Ni3.5(Co0.5Al0.5)x(x=0.0, 0.1, 0.3, 0.5) alloys were prepared by magnetic levitation melting under an Ar atmosphere, and the effects of Co and Al on the hydrogen storage and electrochemical properties were systematically investigated by pressure composition isotherms, cyclic voltammetry, Tafel polarization and electrochemical impedance spectroscopy testing. The results showed that the alloy phases were mainly consisted of (La,Pr)(Ni,Co)5, LaMg2Ni9, (La,Nd)2Ni7 and LaNi3 phases, and the cell volumes of (La,Pr)(Ni,Co)5, LaMg2Ni9, (La,Nd)2Ni7 and LaNi3 phases expanded with Co and Al element added. The hydrogen storage capacity initially increased from 1.36 (x=0) to 1.47 wt.% (x=0.3) and then decreased to 1.22 wt.% (x=0.5). The discharge capacity retention and cycle stability of the alloy electrodes were improved with the increase of Co and Al contents. The La0.55Pr0.05Nd0.15Mg0.25Ni3.5(Co0.5Al0.5)0.3 alloy electrode possessed better electrochemical kinetic characteristic.

详情信息展示

A study on hydrogen storage and electrochemical properties of La0.55Pr0.05Nd0.15Mg0.25Ni3.5 (Co0.5Al0.5)x (x=0.0, 0.1, 0.3, 0.5) alloys

覃铭1,2,蓝志强1,丁杨1,熊凯1,刘奕新1,郭进1

1. College of Physics Science and Technology, Guangxi University2. Department of Physics and Electronic Engineering, Baise University

摘 要:The La0.55Pr0.05Nd0.15Mg0.25Ni3.5(Co0.5Al0.5)x(x=0.0, 0.1, 0.3, 0.5) alloys were prepared by magnetic levitation melting under an Ar atmosphere, and the effects of Co and Al on the hydrogen storage and electrochemical properties were systematically investigated by pressure composition isotherms, cyclic voltammetry, Tafel polarization and electrochemical impedance spectroscopy testing. The results showed that the alloy phases were mainly consisted of (La,Pr)(Ni,Co)5, LaMg2Ni9, (La,Nd)2Ni7 and LaNi3 phases, and the cell volumes of (La,Pr)(Ni,Co)5, LaMg2Ni9, (La,Nd)2Ni7 and LaNi3 phases expanded with Co and Al element added. The hydrogen storage capacity initially increased from 1.36 (x=0) to 1.47 wt.% (x=0.3) and then decreased to 1.22 wt.% (x=0.5). The discharge capacity retention and cycle stability of the alloy electrodes were improved with the increase of Co and Al contents. The La0.55Pr0.05Nd0.15Mg0.25Ni3.5(Co0.5Al0.5)0.3 alloy electrode possessed better electrochemical kinetic characteristic.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号