Sn对Mg-6Al合金力学性能的影响
来源期刊:有色金属2010年第4期
论文作者:李萍
文章页码:1 - 3
关键词:金属材料; Mg-6Al合金; Sn; 抗拉强度; 延伸率
Key words:metal material; Mg-6Al alloy; Sn; tensile strength; elongation
摘 要:采用拉伸试验、断口分析和组织观察,研究150℃和175℃下不同Sn含量Mg-6Al合金的抗拉强度和延伸率,得出Mg-6Al合金的力学性能随Sn含量的变化关系。结果表明,随着Sn含量的增加,Mg-6Al合金的抗拉强度和延伸率均先增加后降低,且均在Sn含量为1%时取得最大值。加入适量的Sn可改善Mg-6Al合金的显微组织,从而提高其力学性能。
Abstract: The tensile strength and elongation of Mg-6Al alloy with different content of Sn at 150℃ and 175℃ are investigated by tensile tests,fracture analysis and microstructure observation,and the relation between Sn and the mechanical properties of Mg-6Al alloy is obtained.The results show that the tensile strength and the elongation of Mg-6Al alloy are increased at first and then decreased with the increase of Sn content.And the peaks appear at 1%Sn.With the suitable content of Sn,the microstructure of Mg-6Al alloy can be improved and the mechanical properties can be promoted.
李萍1
(1.河南省洛阳市洛阳理工学院 土木工程系)
摘 要:采用拉伸试验、断口分析和组织观察,研究150℃和175℃下不同Sn含量Mg-6Al合金的抗拉强度和延伸率,得出Mg-6Al合金的力学性能随Sn含量的变化关系。结果表明,随着Sn含量的增加,Mg-6Al合金的抗拉强度和延伸率均先增加后降低,且均在Sn含量为1%时取得最大值。加入适量的Sn可改善Mg-6Al合金的显微组织,从而提高其力学性能。
关键词:金属材料; Mg-6Al合金; Sn; 抗拉强度; 延伸率