Preparation and Characterization of Chitosan/β-GP Membranes for Guided Bone Regeneration
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第2期
论文作者：崔军 徐欣 孙康宁
文章页码：242 - 246
摘 要：Bioabsorbable chitosan/β-glycerol phosphate （CS/β-GP） composite membranes were fabricated through a relatively PH neutral and mild sol-gel process for guided bone regeneration （GBR）.Their structural properties,morphology,and tensile strength were investigated.FTIR and XRD analyses indicated that there were chemical bonds between the CS andβ-GP.SEM analysis revealed that the CS/β-GP composite membranes had a porous structure both at the surface and in sublayers.Even though the incorporation ofβ-GP in the CS matrix decreased the initial tensile strength of the membrane,the CS/β-GP membranes were still fit for GBR application with their tensile strength of roughly 1MPa.The concentration ofβ-GP was proportional to the pore size and thickness but was inversely proportional to the tensile strength of the CS/β-GP membrane.The present findings indicate that,based on its characteristics,the CS/β-GP composite membrane is a potential bioresorbable membrane for use in guided bone regeneration.
崔军1，徐欣1,2，孙康宁3
1. Department of Dental Implant Center,School of Stomatology,Shandong University3. School of Materials Science and Engineering,Shandong University
摘 要：Bioabsorbable chitosan/β-glycerol phosphate （CS/β-GP） composite membranes were fabricated through a relatively PH neutral and mild sol-gel process for guided bone regeneration （GBR）.Their structural properties,morphology,and tensile strength were investigated.FTIR and XRD analyses indicated that there were chemical bonds between the CS andβ-GP.SEM analysis revealed that the CS/β-GP composite membranes had a porous structure both at the surface and in sublayers.Even though the incorporation ofβ-GP in the CS matrix decreased the initial tensile strength of the membrane,the CS/β-GP membranes were still fit for GBR application with their tensile strength of roughly 1MPa.The concentration ofβ-GP was proportional to the pore size and thickness but was inversely proportional to the tensile strength of the CS/β-GP membrane.The present findings indicate that,based on its characteristics,the CS/β-GP composite membrane is a potential bioresorbable membrane for use in guided bone regeneration.
关键词：