Erosion Resistance Behaviours of H13 Steel to Molten ADC12 Alloy
来源期刊:材料热处理学报2004年第5期
论文作者:WANG Rong WU Xiao-chun LI Lin MIN Yong-an XU Luo-ping
关键词:Erosion resistance,oxide film,hot work steel; aluminium alloy;
摘 要:H13 hot work steel samples and surface water vapor oxidized H13 samples were immersed into molten ADC12alloy under static resting or dynamic rotating conditions. Weigh-losing method was used to discover the influences of temperature, time and surface conditions on the erosion resistance of H13 steel. The interfaces between the steel and the molten alloy were studied with optical microscopy to compare the different erosion resistance behaviours. The results show that the composite layer outside of the compounds layers changes obviously with increasing temperature, lasting time or sample movement. The better erosion resistance of H13 steel can be endowed with the oxide films, which would gradually decrease along with the dissolve of the films.
WANG Rong1,WU Xiao-chun1,LI Lin1,MIN Yong-an1,XU Luo-ping1
(1.School of materials science and Engineering, Shanghai University, Shanghai, China)
摘要:H13 hot work steel samples and surface water vapor oxidized H13 samples were immersed into molten ADC12alloy under static resting or dynamic rotating conditions. Weigh-losing method was used to discover the influences of temperature, time and surface conditions on the erosion resistance of H13 steel. The interfaces between the steel and the molten alloy were studied with optical microscopy to compare the different erosion resistance behaviours. The results show that the composite layer outside of the compounds layers changes obviously with increasing temperature, lasting time or sample movement. The better erosion resistance of H13 steel can be endowed with the oxide films, which would gradually decrease along with the dissolve of the films.
关键词:Erosion resistance,oxide film,hot work steel; aluminium alloy;