Generation Mechanism of Interfacial Layer and Its Effect on Fe-Cr-Ni/Al-Si-Cu-Ni-Mg Composite Performance
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第5期
论文作者：周灵展 YANG Liming ZHU Xiurong PENG Yinjiang
文章页码：1193 - 1198
摘 要：Fe-Cr-Ni/Al-Si-Cu-Ni-Mg composite was taken as the experimental material. The chemical composition of interfacial layer was tested. The generation mechanism and influence of interfacial layer on the composite were analyzed. The results indicated that the generation of interfacial layer is sensitive to temperature. Interfacial layer will generate rapidly when temperature reaches 500 ℃ or above. The interfacial layer is mainly composed of Al, Si, Cu, Fe, and Cr, element Ni distributes at the outward of the interfacial layer for the precipitate of Ni later than Si and Cu, and there is almost no diffusion of Ni during the solution treatment. During heat treatment process, unequal quantity changing of metal atom results in disperse or concentrated vacancies or holes near the matrix. The existence of interfacial layer will induce a decrease of compression strength and plasticity at room temperature and an increase of strength at higher temperature comparing with composite without interfacial layer.
周灵展1,2，YANG Liming1，ZHU Xiurong2，PENG Yinjiang2
1. Faculty of Mechanical Engineering and Mechanics, Ningbo University2. Ningbo Branch of China Ordnance Academy
摘 要：Fe-Cr-Ni/Al-Si-Cu-Ni-Mg composite was taken as the experimental material. The chemical composition of interfacial layer was tested. The generation mechanism and influence of interfacial layer on the composite were analyzed. The results indicated that the generation of interfacial layer is sensitive to temperature. Interfacial layer will generate rapidly when temperature reaches 500 ℃ or above. The interfacial layer is mainly composed of Al, Si, Cu, Fe, and Cr, element Ni distributes at the outward of the interfacial layer for the precipitate of Ni later than Si and Cu, and there is almost no diffusion of Ni during the solution treatment. During heat treatment process, unequal quantity changing of metal atom results in disperse or concentrated vacancies or holes near the matrix. The existence of interfacial layer will induce a decrease of compression strength and plasticity at room temperature and an increase of strength at higher temperature comparing with composite without interfacial layer.