X80热连轧管线钢的成分、工艺对组织及性能的影响
来源期刊:钢铁2009年第4期
论文作者:崔天燮 尚成嘉 缪成亮 薛文广 胡玉亭
文章页码:55 - 59
关键词:X80热连轧管线钢; 平均流变应力; 再结晶; 精轧工艺
Key words:X80 pipeline strip steel; mean flow stress; recrystallization; finish rolling process
摘 要:对三种不同成分设计的Mn-Mo-Nb+钢的精轧轧程、轧制温度以及C、Mo含量对热轧板卷屈服强度和DWTT撕裂面积等性能的影响进行了研究,所得到的结论对提高强度,细化奥氏体晶粒,避免混晶具有指导性。采用含Mo低碳、高Nb设计,控制精轧轧程,可以获得具有优良强度和韧性的X80热连轧管线钢产品。
Abstract: Based on Mn-Mo-Nb system with three different content,the effect of finishing rolling parameters and rolling temperature as well as the content of C and Mo on yield strength and DWTT shear area values of X80 hot strip pipeline steel were investigated.The results are of practical significance to improvement yield strength and to refinement austenite grain size along with to restraint recrystallization during finish rolling.By adjusting the chemical composition and optimizing the process parameters,excellent toughness and high strength can be obtained.
崔天燮1,尚成嘉2,缪成亮3,薛文广4,胡玉亭4
(1.山西省太原市山西太钢不锈钢股份有限公司技术中心
2.北京科技大学 材料科学与工程学院
3.北京科技大学 材料与工程学院,北京 100083
4.山西太钢不锈钢有限公司 技术中心,山西太原 030003)
摘 要:对三种不同成分设计的Mn-Mo-Nb+钢的精轧轧程、轧制温度以及C、Mo含量对热轧板卷屈服强度和DWTT撕裂面积等性能的影响进行了研究,所得到的结论对提高强度,细化奥氏体晶粒,避免混晶具有指导性。采用含Mo低碳、高Nb设计,控制精轧轧程,可以获得具有优良强度和韧性的X80热连轧管线钢产品。
关键词:X80热连轧管线钢; 平均流变应力; 再结晶; 精轧工艺