Octacalcium Phosphate Fiber Synthesized by Homogeneous Precipitation Method
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2010年第5期
论文作者：王小俊 方立明
文章页码：747 - 752
摘 要：Calcium phosphate fiber was synthesized by homogeneous precipitation method using urea as precipitation agent. Effects of the reactant concentration and hydrothermal temperature on the calcium phosphate morphology and composition were studied using SEM, FTIR and XRD. It is found that fine octacalcium phosphate（OCP）fiber can be synthesized when the reactant concentrations are 0.167 mol/L for Ca（NO3）2, 0.1 mol/L for （NH4）2HPO4, and 0.6-0.7 mol/L for （NH2）2CO, respectively, with the initial reactant solution pH value around 2.2, hydrothermal temperature 90 ℃ and termination reaction at pH value around 5.0. At very low urea concentration, the product size distribution is highly inhomogeneous, however, at an excessively high concentration the product becomes larger and shorter and a mixture of OCP and hydroxyapatite （HA）. Increasing the hydrothermal temperature is favorable to the fast precipitation of OCP, higher productivity and finer product.
王小俊1，方立明1,2
1. School of Materials Science and Engineering, South China University of Technology2. National Engineering Research Center for Human Tissue Restoration and Function Reconstruction, South China University of Technology
摘 要：Calcium phosphate fiber was synthesized by homogeneous precipitation method using urea as precipitation agent. Effects of the reactant concentration and hydrothermal temperature on the calcium phosphate morphology and composition were studied using SEM, FTIR and XRD. It is found that fine octacalcium phosphate（OCP）fiber can be synthesized when the reactant concentrations are 0.167 mol/L for Ca（NO3）2, 0.1 mol/L for （NH4）2HPO4, and 0.6-0.7 mol/L for （NH2）2CO, respectively, with the initial reactant solution pH value around 2.2, hydrothermal temperature 90 ℃ and termination reaction at pH value around 5.0. At very low urea concentration, the product size distribution is highly inhomogeneous, however, at an excessively high concentration the product becomes larger and shorter and a mixture of OCP and hydroxyapatite （HA）. Increasing the hydrothermal temperature is favorable to the fast precipitation of OCP, higher productivity and finer product.
关键词：