Proton Conducting Composite Membranes from Sulfonated Polyether Ether Ketone and SiO2
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第1期
论文作者：张高文
文章页码：95 - 99
摘 要：Proton conducting composite membranes from sulfonated polyether ether ketone and SiO2 for direct methanol fuel cell （DMFC） application were prepared with sulfonated polyether ether ketone（SPEEK） and tetracethoxy silane（TEOS） by sol-gel method. The covalent crosslinking structure was formed between —SO3H of SPEEK via SiO2. The SEM images show that the interfacial compatibility of SPEEK and SiO2 is improved obviously and SiO2 disperses uniformly in the polymer matrix and the particle diameter of SiO2 does not exceed 40 nm. The proton conductivity of composite membranes decreases slightly compared with the SPEEK membrane while the methanol permeability and swelling of composite membrane are improved remarkablely owing to covalent cross-linking between —SO3H and SiO2 .
张高文
College of Chemistry and Environment, Hubei University of Technology
摘 要：Proton conducting composite membranes from sulfonated polyether ether ketone and SiO2 for direct methanol fuel cell （DMFC） application were prepared with sulfonated polyether ether ketone（SPEEK） and tetracethoxy silane（TEOS） by sol-gel method. The covalent crosslinking structure was formed between —SO3H of SPEEK via SiO2. The SEM images show that the interfacial compatibility of SPEEK and SiO2 is improved obviously and SiO2 disperses uniformly in the polymer matrix and the particle diameter of SiO2 does not exceed 40 nm. The proton conductivity of composite membranes decreases slightly compared with the SPEEK membrane while the methanol permeability and swelling of composite membrane are improved remarkablely owing to covalent cross-linking between —SO3H and SiO2 .
关键词：