The Phase Transformation of R2O-CaO-SiO2-F Glass-ceramics

来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2010年第1期

论文作者:宋树欣

文章页码:49 - 52

摘    要:The phase transformation of R2O-CaO-SiO2-F system glass-ceramics with various additions of K2O and F was investigated by DTA, XRD, SEM and other techniques. The crystallization and the microstructure of the obtained glass-ceramics were also evaluated. The phase separation occurred in CN1 specimen after being quenched in water, but phase separation did not appear in other quenched specimens with the content of K2O and F increasing obviously, showing K2O and F modified the structure of the glass-forming melts. The increase of K2O and F resulted in the reduction of phase separation and the enhancement of crystallization. The main crystalline phase formed after heat-treatment was canasite and CaF2. The microstructures of the crystalline specimens consisted of interlocking radial and granular crystals. Moreover, the crystallinity was increased as the content of K2O was increased from 0.07 mol to 0.08 mol.

详情信息展示

The Phase Transformation of R2O-CaO-SiO2-F Glass-ceramics

宋树欣

Key Laboratory of Silicate Materials Science and Engineering (Wuhan University of Technology),Ministry of Education

摘 要:The phase transformation of R2O-CaO-SiO2-F system glass-ceramics with various additions of K2O and F was investigated by DTA, XRD, SEM and other techniques. The crystallization and the microstructure of the obtained glass-ceramics were also evaluated. The phase separation occurred in CN1 specimen after being quenched in water, but phase separation did not appear in other quenched specimens with the content of K2O and F increasing obviously, showing K2O and F modified the structure of the glass-forming melts. The increase of K2O and F resulted in the reduction of phase separation and the enhancement of crystallization. The main crystalline phase formed after heat-treatment was canasite and CaF2. The microstructures of the crystalline specimens consisted of interlocking radial and granular crystals. Moreover, the crystallinity was increased as the content of K2O was increased from 0.07 mol to 0.08 mol.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号