Limited Effect of Twin Boundaries on Radiation Damage
来源期刊:Acta Metallurgica Sinica2016年第1期
论文作者:Jin Gao Zhi-Jun Liu Fa-Rong Wan
文章页码:72 - 78
摘 要:The different influences of the general grain boundary and the twin boundary on the cavity formation were investigated in copper irradiated by helium at room temperature.Large number of the cavities with sizes smaller than 5 nm formed after irradiation,which were almost homogenously distributed inside the grains.However,the distribution of the cavities varied near the general grain boundary and the twin boundary.Cavities-depleted zone was readily observed near the general grain boundaries,which was rarely observed near the twin boundaries.Meanwhile,decoration of dense cavities within the grain boundary plane was observed.The results suggested the limited influence of the twin boundaries as the point defect sinks compared with the general grain boundaries.
Jin Gao,Zhi-Jun Liu,Fa-Rong Wan
Department of Materials Physics and Chemistry,School of Materials Science and Engineering,University of Science and Technology Beijing
摘 要:The different influences of the general grain boundary and the twin boundary on the cavity formation were investigated in copper irradiated by helium at room temperature.Large number of the cavities with sizes smaller than 5 nm formed after irradiation,which were almost homogenously distributed inside the grains.However,the distribution of the cavities varied near the general grain boundary and the twin boundary.Cavities-depleted zone was readily observed near the general grain boundaries,which was rarely observed near the twin boundaries.Meanwhile,decoration of dense cavities within the grain boundary plane was observed.The results suggested the limited influence of the twin boundaries as the point defect sinks compared with the general grain boundaries.
关键词: