Effect of mold rotation on the bifilar electroslag remelting process

来源期刊:International Journal of Minerals Metallurgy and Materials2015年第10期

论文作者:Xiao-fang Shi Li-zhong Chang Jian-jun Wang

文章页码:1033 - 1042

摘    要:A novel electroslag furnace with a rotating mold was fabricated, and the effects of mold rotational speed on the electroslag remelting process were investigated. The results showed that the chemical element distribution in ingots became uniform and that their compact density increased when the mold rotational speed was increased from 0 to 28 r/min. These results were attributed to a reasonable mold speed, which resulted in a uniform temperature in the slag pool and scattered the metal droplets randomly in the metal pool. However, an excessive rotational speed caused deterioration of the solidification structure. When the mold rotational speeds was increased from 0 to 28 r/min, the size of Al2O3 inclusions in the electroslag ingot decreased from 4.4 to 1.9 μm. But the excessive mold rotational speed would decrease the ability of the electroslag remelting to remove the inclusions. The remelting speed gradually increased, which resulted in reduced power consumption with increasing mold rotational speed. This effect was attributed to accelerated heat exchange between the consumable electrode and the molten slag, which resulted from mold rotation. Nevertheless, when the rotational speed reached 28 r/min, the remelting speed did not change because of limitations of metal heat conduction. Mold rotation also improved the surface quality of the ingots by promoting a uniform temperature distribution in the slag pool.

详情信息展示

Effect of mold rotation on the bifilar electroslag remelting process

Xiao-fang Shi,Li-zhong Chang,Jian-jun Wang

School of Metallurgy Engineering,Anhui University of Technology

摘 要:A novel electroslag furnace with a rotating mold was fabricated, and the effects of mold rotational speed on the electroslag remelting process were investigated. The results showed that the chemical element distribution in ingots became uniform and that their compact density increased when the mold rotational speed was increased from 0 to 28 r/min. These results were attributed to a reasonable mold speed, which resulted in a uniform temperature in the slag pool and scattered the metal droplets randomly in the metal pool. However, an excessive rotational speed caused deterioration of the solidification structure. When the mold rotational speeds was increased from 0 to 28 r/min, the size of Al2O3 inclusions in the electroslag ingot decreased from 4.4 to 1.9 μm. But the excessive mold rotational speed would decrease the ability of the electroslag remelting to remove the inclusions. The remelting speed gradually increased, which resulted in reduced power consumption with increasing mold rotational speed. This effect was attributed to accelerated heat exchange between the consumable electrode and the molten slag, which resulted from mold rotation. Nevertheless, when the rotational speed reached 28 r/min, the remelting speed did not change because of limitations of metal heat conduction. Mold rotation also improved the surface quality of the ingots by promoting a uniform temperature distribution in the slag pool.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号