Characterization and Thermal Conductivity of Modified Graphite/Fatty Acid Eutectic/PMMA Form-Stable Phase Change Material
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2013年第3期
论文作者：孟多 WANG Lijiu
文章页码：586 - 591
摘 要：We prepared and characterized a form-stable composite phase change material （PCM） with higher thermal conductivity. Capric acid（CA）-myristic acid（MA） eutectic as core, poly-methyl methacrylate （PMMA） as supportive matrix and modified graphite （MG） powders serving as the thermal conductance improver were blended by bulk- polymerization method. The composite PCMs with different MG mass fraction （2%, 5%, 7%, 10% and 15%） were characterized by FT-IR, SEM, DSC technique and mechanical tests. Thermal conductivities of the composites were measured by transient hot-wire method. The results indicate that MG powders have been successfully inserted into the CA-MA/PMMA matrix without any chemical reaction with each other. The MG/CA-MA/PMMA composites maintain good thermal storage performance while the thermal conductivity has been enhanced significantly. The composite PCM added with 15 wt% MG powders increases approximately as 195.9% in thermal conductivity. Moreover, the thermal conductivity improvement of the composite PCMs is also verified by the melting-freezing experiment, which is profitable for the heat transfer efficiency in latent heat thermal energy storage system.
孟多1，WANG Lijiu2
1. School of Civil and Architectural Engineering, Liaoning University of Technology2. Institute of Building Materials, Dalian University of Technology
摘 要：We prepared and characterized a form-stable composite phase change material （PCM） with higher thermal conductivity. Capric acid（CA）-myristic acid（MA） eutectic as core, poly-methyl methacrylate （PMMA） as supportive matrix and modified graphite （MG） powders serving as the thermal conductance improver were blended by bulk- polymerization method. The composite PCMs with different MG mass fraction （2%, 5%, 7%, 10% and 15%） were characterized by FT-IR, SEM, DSC technique and mechanical tests. Thermal conductivities of the composites were measured by transient hot-wire method. The results indicate that MG powders have been successfully inserted into the CA-MA/PMMA matrix without any chemical reaction with each other. The MG/CA-MA/PMMA composites maintain good thermal storage performance while the thermal conductivity has been enhanced significantly. The composite PCM added with 15 wt% MG powders increases approximately as 195.9% in thermal conductivity. Moreover, the thermal conductivity improvement of the composite PCMs is also verified by the melting-freezing experiment, which is profitable for the heat transfer efficiency in latent heat thermal energy storage system.
关键词：