Zn1-xCoxO Diluted Magnetic Semiconductor Bulk Prepared by Hot Pressing
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2010年第3期
论文作者：林文松
文章页码：527 - 529
摘 要：Zn1-xCoxO diluted magnetic semiconductor bulks were prepared by hot pressing.Mixed powders of pure ZnO and CoO were compacted under pressure of 10 MPa at the temperature of 1 073 K.Then the samples were annealed in vacuum at the temperature from 673 K to 873 K for 10 h.The crystal structure and magnetic properties of Zn1-xCoxO bulks have been investigated by X-ray diffraction（XRD） and vibrating sample magnetometer（VSM）.X-ray photoelectron spectroscopy（XPS） was used to study chemical valence of zinc and cobalt in the samples.The results showed that Zn1-xCoxO samples had c-axis oriented wurtzite symmetry,neither cobalt or cobalt oxide phase was found in the samples if x was less than 0.15.Zn and Co existed in Zn0.9Co0.1O sample in Zn2+ and Co2+ states.The results of VSM experiment proved the room temperature ferromagnetic properties（RTFP） of Co-doped ZnO samples.The saturation magnetization and the coercivity of Zn0.9Co0.1O sample,observed in the M-H curve,were about 0.20 emu/g and 200 Oe,respectively.
林文松
School of Materials Engineering,Shanghai University of Engineering Science
摘 要：Zn1-xCoxO diluted magnetic semiconductor bulks were prepared by hot pressing.Mixed powders of pure ZnO and CoO were compacted under pressure of 10 MPa at the temperature of 1 073 K.Then the samples were annealed in vacuum at the temperature from 673 K to 873 K for 10 h.The crystal structure and magnetic properties of Zn1-xCoxO bulks have been investigated by X-ray diffraction（XRD） and vibrating sample magnetometer（VSM）.X-ray photoelectron spectroscopy（XPS） was used to study chemical valence of zinc and cobalt in the samples.The results showed that Zn1-xCoxO samples had c-axis oriented wurtzite symmetry,neither cobalt or cobalt oxide phase was found in the samples if x was less than 0.15.Zn and Co existed in Zn0.9Co0.1O sample in Zn2+ and Co2+ states.The results of VSM experiment proved the room temperature ferromagnetic properties（RTFP） of Co-doped ZnO samples.The saturation magnetization and the coercivity of Zn0.9Co0.1O sample,observed in the M-H curve,were about 0.20 emu/g and 200 Oe,respectively.
关键词：