Brazing 6061 aluminum alloy with Al-Si-Zn filler metals containing Sr
来源期刊：International Journal of Minerals Metallurgy and Materials2013年第4期
论文作者：Wei Dai Song-bai Xue Feng Ji Jiang Lou Bo Sun Shui-qing Wang
文章页码：365 - 370
摘 要：Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joints were investigated. It was found that zinc in the Al-Si filler metals could reduce the formation of eutectic Al-Si phase and lower the brazing temperature at about 520℃. Adding 0.09wt% Sr element into the Al-6.5Si-42Zn alloy caused α-Al phase refinement and transformed acicular Si phase into the finely fiber-like. After water cooling, Zn element dissolved into the Al-Si eutectic area, and η-Zn phase disappeared in the brazed joints. Tensile strength testing results showed that the Sr-modified filler metal could enhance the strength of the brazed joints by 13% than Al-12Si, while water-cooling further improved the strength at 144 MPa.
Wei Dai1，Song-bai Xue1，Feng Ji1，Jiang Lou2，Bo Sun2，Shui-qing Wang2
1. School of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics2. Zhejiang Xinrui Welding Material Co., Ltd
摘 要：Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joints were investigated. It was found that zinc in the Al-Si filler metals could reduce the formation of eutectic Al-Si phase and lower the brazing temperature at about 520℃. Adding 0.09wt% Sr element into the Al-6.5Si-42Zn alloy caused α-Al phase refinement and transformed acicular Si phase into the finely fiber-like. After water cooling, Zn element dissolved into the Al-Si eutectic area, and η-Zn phase disappeared in the brazed joints. Tensile strength testing results showed that the Sr-modified filler metal could enhance the strength of the brazed joints by 13% than Al-12Si, while water-cooling further improved the strength at 144 MPa.
关键词：