Optimization of the heat treatment of additively manufactured Ni-base superalloy IN718
来源期刊：International Journal of Minerals Metallurgy and Materials2020年第5期
论文作者：Benedikt Diepold Nora Vorlaufer Steffen Neumeier Mathias G?ken
文章页码：640 - 648
摘 要：Additive manufacturing（AM） of Ni-base superalloy components can lead to a significant reduction of weight in aerospace applications. AM of IN718 by selective laser melting results in a very fine dendritic microstructure with a high dislocation density due to the fast solidification process. The complex phase composition of this alloy, with three different types of precipitates and high residual stresses, necessitates adjustment of the conventional heat treatment for AM parts. To find an optimized heat treatment, the microstructures and mechanical properties of differently solution heat-treated samples were investigated by transmission and scanning electron microscopy, including electron backscatter diffraction, and compression tests. After a solution heat treatment（SHT）, the Nb-rich Laves phase dissolves and the dislocation density is reduced, which eliminates the dendritic substructure. SHT at 930 or 954°C leads to the precipitation of the δ-phase, which reduces the volume fraction of the strengthening γ′-and γ′′-phases formed during the subsequent two stage aging treatment. With a higher SHT temperature of 1000°C, where no δ-phase is precipitated, higher γ′ and γ′′ volume fractions are achieved, which results in the optimum strength of all of the solution heat treated conditions.
Benedikt Diepold1，Nora Vorlaufer1，Steffen Neumeier1，Mathias G?ken1
1. Department of Materials Science & Engineering, Institute I, Friedrich-Alexander-Universit?t Erlangen-Nürnberg
摘 要：Additive manufacturing（AM） of Ni-base superalloy components can lead to a significant reduction of weight in aerospace applications. AM of IN718 by selective laser melting results in a very fine dendritic microstructure with a high dislocation density due to the fast solidification process. The complex phase composition of this alloy, with three different types of precipitates and high residual stresses, necessitates adjustment of the conventional heat treatment for AM parts. To find an optimized heat treatment, the microstructures and mechanical properties of differently solution heat-treated samples were investigated by transmission and scanning electron microscopy, including electron backscatter diffraction, and compression tests. After a solution heat treatment（SHT）, the Nb-rich Laves phase dissolves and the dislocation density is reduced, which eliminates the dendritic substructure. SHT at 930 or 954°C leads to the precipitation of the δ-phase, which reduces the volume fraction of the strengthening γ′-and γ′′-phases formed during the subsequent two stage aging treatment. With a higher SHT temperature of 1000°C, where no δ-phase is precipitated, higher γ′ and γ′′ volume fractions are achieved, which results in the optimum strength of all of the solution heat treated conditions.
关键词：