纳米晶低钼高铁Fe-Ni-Mo合金的制备及其微观结构

来源期刊:中南大学学报(自然科学版)2006年第4期

论文作者:罗北平 龚竹青 任碧野 杨余芳 陈梦君

文章页码:692 - 697

关键词:电沉积;纳米晶; Fe-Ni-Mo合金;表面形貌;微观结构

Key words:electrodeposition; nanocrystalline; Fe-Ni-Mo alloys; surface morphology; microstructure

摘    要:在酸性柠檬酸盐镀液中电沉积制备低Mo高Fe含量的Fe-Ni-Mo合金;采用扫描电镜、X射线衍射仪和X射线能谱仪对镀层微观结构、表面形貌及组成进行分析。结果表明:工艺条件和钼酸钠浓度对合金组成的影响较大;所得合金晶粒尺寸为6.2~12.7 nm,并随电流密度、温度和电镀液的pH值的改变而变化;合金的晶体生长符合晶核三维生长模型,镀层表面形貌由平行和垂直于基体的生长速度的相对大小决定;镀层物相为固溶体和金属间化合物的多相结构,当电流密度为3 A/dm2时,镀层物相由FeNi(BCC)和FeMo固溶相转化为FeNi(FCC)和 MoNi4多相结构;镀层的应力随晶粒尺寸的减小呈线性增大;合金镀层的点阵常数发生了畸变。

Abstract: Nanocrystalline Fe-Ni-Mo alloy with low Mo and high Fe content was electrodeposited from acid citrate electrolyte. The surface morphology, microstructure and composition of the alloys were analyzed by scanning electron microscopy, X-ray diffactometry and energy dispersive spectrometry. The results show that the technical parameters and the concentration of sodium molybdate have obvious effect on the composition of the alloy. The crystal grain size is from 6.2 to 12.7 nm and changes with current density, temperature and the pH value of the electrolyte.The crystalline growth of the alloy accords with the model of three-dimensional growth. The surface morphology is mainly determined by the rate competitions between the growing direction of vertical surface and the expanding direction along the surface towards circumambient. The results of the X-ray data show the presence of the multiphase containing solid solution and intermetallic compound in the deposits. The deposit phases alter from the FeNi(BCC) and FeMo solid solution to the FeNi(FCC) and MoNi4structure at 3 A/dm2. The deposits internal stress increases linearly with the decrease of the grain size. The lattice parameter of the deposits are slightly distorted because of the residual stress in the deposits.

详情信息展示

 

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号