Interface modification of Al18B4O33w/6061Al composite by CuO coating on whisker surface
来源期刊：Rare Metals2007年第S1期
论文作者：GAO Haiqi,WANG Lidong and FEI Weidong,School of Materials Science and Engineering,Harbin Institute of Technology,Harbin ,China
文章页码：46 - 50
摘 要：Copper coating was deposited on the surface of aluminum borate whisker（denoted by Al18B4O33w） by an electroless plating method.The result of X-ray diffraction（XRD） of whisker sintered at 850 ℃ indicates that CuO peaks can be found clearly.This method was used to modify the interface properties of the Al18B4O33w reinforced 6061Al matrix composite.Scanning electron microscope（SEM） observation indicates that the uniform coating can be obtained on the whisker surface.Transmission electron microscope（TEM） observation indicates the brittle spinel product（MgAl2O4） between Al18B4O33w and 6061Al matrix,the structure continuity of the whisker are greatly destroyed after the squeeze-casting process and heat treatment.Although copper coating can not totally hinder the spinel reaction,it effectively constrains the spinel reaction and preserves the structure integrity of the Al18B4O33w.
GAO Haiqi,WANG Lidong and FEI Weidong,School of Materials Science and Engineering,Harbin Institute of Technology,Harbin 150001,China
摘 要：Copper coating was deposited on the surface of aluminum borate whisker（denoted by Al18B4O33w） by an electroless plating method.The result of X-ray diffraction（XRD） of whisker sintered at 850 ℃ indicates that CuO peaks can be found clearly.This method was used to modify the interface properties of the Al18B4O33w reinforced 6061Al matrix composite.Scanning electron microscope（SEM） observation indicates that the uniform coating can be obtained on the whisker surface.Transmission electron microscope（TEM） observation indicates the brittle spinel product（MgAl2O4） between Al18B4O33w and 6061Al matrix,the structure continuity of the whisker are greatly destroyed after the squeeze-casting process and heat treatment.Although copper coating can not totally hinder the spinel reaction,it effectively constrains the spinel reaction and preserves the structure integrity of the Al18B4O33w.
关键词：