热轧工艺对430铁素体不锈钢黏结行为的影响
来源期刊:钢铁2011年第5期
论文作者:杨连宏 刘雅政 周乐育
文章页码:56 - 59
关键词:铁素体不锈钢; 热轧; 黏结机制
Key words:ferrite stainless steel; hot rolling; sticking mechanism
摘 要:430铁素体不锈钢在热轧期间易出现黏结现象。针对黏结现象对带钢表面质量的不良影响,分析了热轧期间出现黏结行为的机制,讨论了影响黏结行为的热轧工艺条件,并提出了针对性的措施。通过采用适宜的工艺条件,如选用具有较高表面光洁度的高速钢轧辊,减少轧制过程中的除鳞与冷却,减小粗轧送料厚度,并采用适当的工艺润滑条件,可有效抑制黏结现象的发生。
Abstract: Sticking phenomenon often occurs during hot-rolling process of 430 ferrite stainless steel.Aim to the bad influence of sticking on surface quality of strip,sticking mechanism of 430 ferrite stainless steel during hot-rolling was analyzed,effect of hot-rolling process parameter on sticking behavior was discussed,and some measures were put forward.By appropriate process conditions,such as using high speed steel(HSS) roller,reduction of descaling and cooling during hot-rolling,decreasing the thickness of medium slab,and adopting appropriate lubrication,the sticking phenomenon of 430 ferrite stainless steel was restrained effectively.
杨连宏1,2,刘雅政1,周乐育2
(1.北京市北京科技大学材料科学与工程学院
2.山西省太原市太原钢铁(集团)有限公司)
摘 要:430铁素体不锈钢在热轧期间易出现黏结现象。针对黏结现象对带钢表面质量的不良影响,分析了热轧期间出现黏结行为的机制,讨论了影响黏结行为的热轧工艺条件,并提出了针对性的措施。通过采用适宜的工艺条件,如选用具有较高表面光洁度的高速钢轧辊,减少轧制过程中的除鳞与冷却,减小粗轧送料厚度,并采用适当的工艺润滑条件,可有效抑制黏结现象的发生。
关键词:铁素体不锈钢; 热轧; 黏结机制