Effect of Isobutyl-triethoxy-silane Penetrative Protective Agent on the Carbonation Resistance of Concrete
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2016年第1期
论文作者：徐强 詹树林 XU Bingzheng YANG Hui QIAN Xiaoqian DING Xiaofu
文章页码：139 - 145
摘 要：Effect of isobutyl-triethoxy-silane penetrative protective agent on the carbonation resistance of the concrete was studied.The concrete specimens for the 28 d accelerated carbonation process were manufactured with w/c of 0.49 and 0.64,both in the presence and absence of silane and mineral admixture.The penetration of isobutyl-triethoxy-silane and the carbonation of concrete were investigated by penetration depth,carbonation depth,XRD,SEM,and pore size distribution.The results showed that concrete compactness played an important role in the silane penetration and carbonation resistance.Penetration depth of silane-treated concrete mainly depended on the compactness of the concrete,and could not remarkably change through the accelerated carbonation process.In the accelerated carbonation process,penetrative protective agent improved the carbonation resistance of the higher compactness concretes but accelerated the carbonization process of the lower compactness concretes.As penetrative protective agent penetrated along the external connectivity pores into concrete not filling the entire surface area,the inorganic film could not fully protect the Ca（OH）2 phase from carbonation.After 28 d accelerated carbonation,fibrous hydration products disappeared and the surface holes decreased.Due to the formation of carbonized products,the porosity of the concrete surface decreased,especially in high-strength concrete.
徐强1,2，詹树林1，XU Bingzheng2，YANG Hui2,3，QIAN Xiaoqian1，DING Xiaofu4
1. College of Civil Engineering and Architecture,Zhejiang University2. Department of Materials Science and Engineering,Zhejiang University3. Zhejiang-California International Nano Systems Institute4. Zhejiang Heli New Building Materials Co.,Ltd
摘 要：Effect of isobutyl-triethoxy-silane penetrative protective agent on the carbonation resistance of the concrete was studied.The concrete specimens for the 28 d accelerated carbonation process were manufactured with w/c of 0.49 and 0.64,both in the presence and absence of silane and mineral admixture.The penetration of isobutyl-triethoxy-silane and the carbonation of concrete were investigated by penetration depth,carbonation depth,XRD,SEM,and pore size distribution.The results showed that concrete compactness played an important role in the silane penetration and carbonation resistance.Penetration depth of silane-treated concrete mainly depended on the compactness of the concrete,and could not remarkably change through the accelerated carbonation process.In the accelerated carbonation process,penetrative protective agent improved the carbonation resistance of the higher compactness concretes but accelerated the carbonization process of the lower compactness concretes.As penetrative protective agent penetrated along the external connectivity pores into concrete not filling the entire surface area,the inorganic film could not fully protect the Ca（OH）2 phase from carbonation.After 28 d accelerated carbonation,fibrous hydration products disappeared and the surface holes decreased.Due to the formation of carbonized products,the porosity of the concrete surface decreased,especially in high-strength concrete.
关键词：