RELATION BETWEEN HYDRATION PHASE AND PORE STRUCTURE OF SOREL CEMENT AND ITS MACRO PROPERTIES
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition1997年第3期
论文作者：崔崇
文章页码：6 - 11
摘 要：<正>The hydration phase of Sorel cement slurrycompounded at different halogenide ratios was determined bya quantitative XRD method,the pore distribution in Sorel ce-ment was measured by mercury-squashed machine.The resultsshow that the strength of the product increases and the porosi-ty decreases as the amount of 5·1·8 phase increases.Thestructure of slurry blended at ratios of 5·1·8 and 3·1·8shows that the porosity reduces,crystal size grows and most-probability radius of pores decreases as the reaction age pro-longs.The growth of 5·1·8and 3·1·8 phases isfavorable for compactness of the mortar and the porosity isin close relationship with the strength.
崔崇
摘 要：<正>The hydration phase of Sorel cement slurrycompounded at different halogenide ratios was determined bya quantitative XRD method,the pore distribution in Sorel ce-ment was measured by mercury-squashed machine.The resultsshow that the strength of the product increases and the porosi-ty decreases as the amount of 5·1·8 phase increases.Thestructure of slurry blended at ratios of 5·1·8 and 3·1·8shows that the porosity reduces,crystal size grows and most-probability radius of pores decreases as the reaction age pro-longs.The growth of 5·1·8and 3·1·8 phases isfavorable for compactness of the mortar and the porosity isin close relationship with the strength.
关键词：