Ti、Nb对超低碳Cr18铁素体不锈钢冷轧板再结晶织构的影响
来源期刊:钢铁2009年第6期
论文作者:孙丹 陈伟庆 郑宏光
文章页码:81 - 84
关键词:Ti; Nb; Cr18; 铁素体不锈钢; 再结晶织构
Key words:titanium; niobium; Cr18; ferrite stainless steel; recrystallization texture
摘 要:研究了添加Ti、Nb对超低碳Cr18铁素体不锈钢冷轧板再结晶织构的影响。试验结果表明,Nb单稳定化和Ti、Nb双稳定化的冷轧板试样在850℃下,随退火保温时间的延长,{111}面织构取向密度增加,而Ti单稳定的冷轧板在退火2min时{111}面织构取向密度值达到最大,然后随保温时间延长{111}面织构密度下降。Ti、Nb双稳定化的冷轧板经退火360s后得到最大的{111}<112>织构取向密度强度,Nb单稳定化Cr18不锈钢冷轧板再结晶织构{111}取向密度低于其它两种钢。
Abstract: The influence of Ti、Nb on recrystallization texture of the cold rolled sheets of Cr18 stainless steel with ultra-low carbon and nitrogen were studied.The results show that the density of the {111} texture distribution of the Nb-stabilized and Ti、Nb double stabilized cold rolled sheet increase with extending of the annealing time under 850 ℃,but the density of {111} texture of only Ti-stabilized cold rolled sheets are already to maximum with 2 min holding time,then the density of the {111} texture distribution will decline.The density of {111}<110> orientation distribution of the Ti、Nb double stabilized cold rolled sheet reaches the strongest level when annealing time is 360 s.The density of {111} orientation distribution of Nb-stabilized Cr18 stainless steel cold rolled sheet is weaker than the others.
孙丹1,陈伟庆1,郑宏光2
(1.北京市北京科技大学 冶金与生态工程学院
2.宝钢股份不锈钢技术中心,上海 200431)
摘 要:研究了添加Ti、Nb对超低碳Cr18铁素体不锈钢冷轧板再结晶织构的影响。试验结果表明,Nb单稳定化和Ti、Nb双稳定化的冷轧板试样在850℃下,随退火保温时间的延长,{111}面织构取向密度增加,而Ti单稳定的冷轧板在退火2min时{111}面织构取向密度值达到最大,然后随保温时间延长{111}面织构密度下降。Ti、Nb双稳定化的冷轧板经退火360s后得到最大的{111}<112>织构取向密度强度,Nb单稳定化Cr18不锈钢冷轧板再结晶织构{111}取向密度低于其它两种钢。
关键词:Ti; Nb; Cr18; 铁素体不锈钢; 再结晶织构