Microstructure and Mechanical Properties of Intercritical Heat-affected Zone of X80 Pipeline Steel in Simulated In-Service Welding
来源期刊：Acta Metallurgica Sinica2015年第7期
论文作者：Xin-Jie Di Lin Cai Xi-Xue Xing Cui-Xin Chen Zhen-Kui Xue
文章页码：883 - 891
摘 要：The intercritical heat-affected zone（ICHAZ） of X80 pipeline steel was simulated by using the Gleeble-3500thermal/mechanical simulator according to the thermal cycle of in-service welding.The microstructures of ICHAZ with different cooling rates were examined,and the hardness,the toughness and corresponding fractography were investigated.Results show that untransformed bainite and ferrite as well as retransformed fine bainite and martensite–austenite（M–A）constituents constitute the microstructure of ICHAZ.The two different morphologies of M–A constituents are stringer and block.Second phase particles which mainly composed of Ti,Nb,C,Fe and Cu coarsened in ICHAZ.Compared with normal welding condition,the toughness of ICHAZ is poor when the cooling time is short under in-service welding condition because of the large area fraction and size of M–A constituents that connect into chains and distribute at the grain boundaries.The Vickers hardness of ICHAZ that decreases with the increase in the cooling time is independent with the area fraction of M–A constituents.
Xin-Jie Di1,2，Lin Cai1,2，Xi-Xue Xing1,2，Cui-Xin Chen3，Zhen-Kui Xue4
1. School of Materials Science and Engineering,Tianjin University2. Tianjin Key Laboratory of Advanced Joining Technology3. School of Materials Science and Engineering,Hebei University of Technology4. China Petrolum Pipeline Bureau
摘 要：The intercritical heat-affected zone（ICHAZ） of X80 pipeline steel was simulated by using the Gleeble-3500thermal/mechanical simulator according to the thermal cycle of in-service welding.The microstructures of ICHAZ with different cooling rates were examined,and the hardness,the toughness and corresponding fractography were investigated.Results show that untransformed bainite and ferrite as well as retransformed fine bainite and martensite–austenite（M–A）constituents constitute the microstructure of ICHAZ.The two different morphologies of M–A constituents are stringer and block.Second phase particles which mainly composed of Ti,Nb,C,Fe and Cu coarsened in ICHAZ.Compared with normal welding condition,the toughness of ICHAZ is poor when the cooling time is short under in-service welding condition because of the large area fraction and size of M–A constituents that connect into chains and distribute at the grain boundaries.The Vickers hardness of ICHAZ that decreases with the increase in the cooling time is independent with the area fraction of M–A constituents.
关键词：