Crystallographic and electrochemical characteristics of melt-spun Ti-Zr-Ni-Cu alloys
来源期刊：Rare Metals2007年第5期
论文作者：LIU Baozhong,),WU Yaoming),and WANG Limin) ) State Key Laboratory for Application of the Rare Earth Resources,Changchun Institute of Applied Chemistry,Chinese Academy of Sciences,Changchun ,China ) Graduate School of Chinese Academy of Sciences,Beijing ,China
文章页码：440 - 444
摘 要：Ti44Zr32Ni22Cu2 and Ti41Zr29Ni28Cu2 alloys were prepared by the melt-spinning method. The phase structure was analyzed by X-ray diffraction,and the electrochemical performances of the melt-spun alloys were investigated. The results indicated that the Ti44Zr32Ni22Cu2 alloy was composed of the icosahedral quasicrystals and amorphous phases,and the Ti41Zr29Ni28Cu2 alloy comprised icosahedral quasicrystals,amorphous,and Laves phases. The maximum discharge capacity was 141 mAh/g for the Ti44Zr32Ni22Cu2 alloy and 181 mAh/g for the Ti41Zr29Ni28Cu2 alloy,respectively. The Ti41Zr29Ni28Cu2 alloy also showed a better high-rate dischargeability and cycling stability. The better electrochemical prop-erties should be ascribed to the high content of Ni,which was beneficial to the electrochemical kinetic properties and made the alloy more resistant to oxidation,as well as to the Laves phase in the Ti41Zr29Ni28Cu2 alloy,which could work as the electro-catalyst and the micro-current collector.
摘要：Ti44Zr32Ni22Cu2 and Ti41Zr29Ni28Cu2 alloys were prepared by the melt-spinning method. The phase structure was analyzed by X-ray diffraction,and the electrochemical performances of the melt-spun alloys were investigated. The results indicated that the Ti44Zr32Ni22Cu2 alloy was composed of the icosahedral quasicrystals and amorphous phases,and the Ti41Zr29Ni28Cu2 alloy comprised icosahedral quasicrystals,amorphous,and Laves phases. The maximum discharge capacity was 141 mAh/g for the Ti44Zr32Ni22Cu2 alloy and 181 mAh/g for the Ti41Zr29Ni28Cu2 alloy,respectively. The Ti41Zr29Ni28Cu2 alloy also showed a better high-rate dischargeability and cycling stability. The better electrochemical prop-erties should be ascribed to the high content of Ni,which was beneficial to the electrochemical kinetic properties and made the alloy more resistant to oxidation,as well as to the Laves phase in the Ti41Zr29Ni28Cu2 alloy,which could work as the electro-catalyst and the micro-current collector.
关键词：