The Overcoat Oil Lubrication of Microarc Oxidation Coating on Al Alloy by Liquid Plasma Technique
来源期刊:材料保护2004年增刊第2期
论文作者:LUO Zhuang-zi TIAN Jun ZHANG Zhao-zhu WANG Wen-jing LIU Wei-ming
关键词:micro-arc oxidation coating; al alloy; oil lubricating; wear;
摘 要:Ceramic coatings were deposited on 2Al2 alloy with a 100 kW micro-arc oxidation equipment consisting of a potential adjustable ac power supply and alkali electrolyte. The structure of the micro-arc oxidiation coatings was examined using scanning electron microscopy and transmission electron microscopy. The tribological properties of the coatings sliding against steel under the drop and adsorption lubrication of liquid paraffin were evaluated with a Timken tester. The lower friction coefficient of 0.14 and longer wear life of 2450 m of overcoat were observed for the polished micro-arc oxidation coating of 180μm thick at a sliding speed 2. 50 m/s and load 1500 N. This is because the coating has an interlayer of suitable porosity and thickness, which helps to improve the deposition of lubricants and endure the higher load. In other words, the oil is able to adsorb in the porous holes of the overcoat and provided the lubrication of micro reservoir during friction, and the compact and relatively hard interlayer of oxidation coating is able to support heavy load and prevent the oil lubricating film from damage.
LUO Zhuang-zi1,TIAN Jun1,ZHANG Zhao-zhu1,WANG Wen-jing1,LIU Wei-ming1
(1.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, P. R. China)
摘要:Ceramic coatings were deposited on 2Al2 alloy with a 100 kW micro-arc oxidation equipment consisting of a potential adjustable ac power supply and alkali electrolyte. The structure of the micro-arc oxidiation coatings was examined using scanning electron microscopy and transmission electron microscopy. The tribological properties of the coatings sliding against steel under the drop and adsorption lubrication of liquid paraffin were evaluated with a Timken tester. The lower friction coefficient of 0.14 and longer wear life of 2450 m of overcoat were observed for the polished micro-arc oxidation coating of 180μm thick at a sliding speed 2. 50 m/s and load 1500 N. This is because the coating has an interlayer of suitable porosity and thickness, which helps to improve the deposition of lubricants and endure the higher load. In other words, the oil is able to adsorb in the porous holes of the overcoat and provided the lubrication of micro reservoir during friction, and the compact and relatively hard interlayer of oxidation coating is able to support heavy load and prevent the oil lubricating film from damage.