Effect of Shot Blasting on Oxidation Behavior of TP304H Steel at 610℃ -770℃ in Water Vapor
来源期刊：材料热处理学报2004年第5期
论文作者：FU Min
关键词：vapor oxidation; diffusion; TP304H steel; shot blasting;
摘 要：Shot blasting on a tube steel of TP304H can greatly improve the oxidation resistance at 650℃-770℃ in water vapor, by the presence of an appropriate blasting intensity. SEM and EPMA analysis indicated that the structure of the oxide scale turned from multi-layer to monolayer after blasting and Cr2O3 in predominant. The untreated sample characterized in multi-layer oxide was composed of Fe in the outer layer and Fe and Cr underneath. For blasted one, the increase of diffusion rate of Cr and the decrease of effective diffusion energy of scale led to a uniform Cr-rich oxide layer, which was dense and protective and the oxidation resistance was increased.
FU Min1，HE Ja-wen2，LI Xin-geng1
(1.Shandong Electric Power Research Institute of China, Jinan, China;
2.State Key Laboratory for Mechanical Behavior of Materials, Xi'an Jiaotong University, Xi' an, China)
摘要:Shot blasting on a tube steel of TP304H can greatly improve the oxidation resistance at 650℃-770℃ in water vapor, by the presence of an appropriate blasting intensity. SEM and EPMA analysis indicated that the structure of the oxide scale turned from multi-layer to monolayer after blasting and Cr2O3 in predominant. The untreated sample characterized in multi-layer oxide was composed of Fe in the outer layer and Fe and Cr underneath. For blasted one, the increase of diffusion rate of Cr and the decrease of effective diffusion energy of scale led to a uniform Cr-rich oxide layer, which was dense and protective and the oxidation resistance was increased.
关键词:vapor oxidation; diffusion; TP304H steel; shot blasting;
【全文内容正在添加中】