Preparation and tensile properties of DD5 single crystal castings
来源期刊：International Journal of Minerals Metallurgy and Materials2016年第6期
论文作者：Xiang-feng Liang Yu-tao Zhao Zhi-hong Jia Chi Zhang
文章页码：683 - 690
摘 要：The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior examination. The results show that the grain orientation is optimized by constraining the spiral crystallizer in [001] orientation and spatial scale. Also, the γ’ phase of inter-dendrites is larger and more irregular than that in dendrite arms. High temperature tensile tests of DD5 single crystal castings exhibit that the peak stress increases with increasing temperature, while the area reduction shows an opposite trend, when the temperature is below 800°C; meanwhile, when the temperature is between 800°C and 1000°C, the fracture stress of the alloy is the same as the peak stress. The fracture mode changes from shear to ductile with increasing temperature from 600°C and 1000°C.
Xiang-feng Liang，Yu-tao Zhao，Zhi-hong Jia，Chi Zhang
School of Material Science and Engineering, Jiangsu University
摘 要：The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior examination. The results show that the grain orientation is optimized by constraining the spiral crystallizer in [001] orientation and spatial scale. Also, the γ’ phase of inter-dendrites is larger and more irregular than that in dendrite arms. High temperature tensile tests of DD5 single crystal castings exhibit that the peak stress increases with increasing temperature, while the area reduction shows an opposite trend, when the temperature is below 800°C; meanwhile, when the temperature is between 800°C and 1000°C, the fracture stress of the alloy is the same as the peak stress. The fracture mode changes from shear to ductile with increasing temperature from 600°C and 1000°C.
关键词：