Experimental investigation of eutectic point in Al-rich Al-La, Al-Ce, Al-Pr and Al-Nd systems
来源期刊：JOURNAL OF RARE EARTHS2017年第10期
论文作者：曹祖军 孔纲 车淳山 王彦启 彭浩棠
文章页码：1022 - 1028
摘 要：In order to confirm the eutectic composition, eutectic temperature and phases of Al-rich Al-RE（La, Ce, Pr, Nd） binary systems, the eutectic Al-RE alloys with the controversial compositions were investigated. The scanning electron microscopy/energy dispersive spectroscopy（SEM/EDS）, differential scanning calorimetric（DSC） and cooling curve tests analysis indicated that a similar eutectic composition（12 wt.% RE） on the Al-rich region was observed in the Al-La, Al-Ce, Al-Pr and Al-Nd alloys, and the eutectic structure of the alloys was consisted of α-Al and α-Al11RE3 phases by combining with X-ray diffraction（XRD） tests. In addition, the eutectic temperatures determined by DSC and cooling curve tests were very close and around 645 oC.
曹祖军，孔纲，车淳山，王彦启，彭浩棠
School of Materials Science and Engineering, South China University of Technology
摘 要：In order to confirm the eutectic composition, eutectic temperature and phases of Al-rich Al-RE（La, Ce, Pr, Nd） binary systems, the eutectic Al-RE alloys with the controversial compositions were investigated. The scanning electron microscopy/energy dispersive spectroscopy（SEM/EDS）, differential scanning calorimetric（DSC） and cooling curve tests analysis indicated that a similar eutectic composition（12 wt.% RE） on the Al-rich region was observed in the Al-La, Al-Ce, Al-Pr and Al-Nd alloys, and the eutectic structure of the alloys was consisted of α-Al and α-Al11RE3 phases by combining with X-ray diffraction（XRD） tests. In addition, the eutectic temperatures determined by DSC and cooling curve tests were very close and around 645 oC.
关键词：