Preparation and performance of Pr-doped Ba0.5Sr0.5Co0.8Fe0.2O3-δ cathode for IT-SOFCs

来源期刊:Journal of Rare Earths2011年第11期

论文作者:朱成军 衣翠珊 潮洛蒙

文章页码:1070 - 1074

摘    要:(Ba0.5Sr0.5)1-xPrxCo0.8Fe0.2O3-δ(BSPCFx;x=0.00-0.30) oxides were synthesized by a sol-gel thermolysis process using combination of PVA and urea,and were also investigated as cathode material for intermediate temperature solid oxide fuel cells(IT-SOFCs).X-ray diffraction(XRD) results showed that all the samples formed a single phase cubic pervoskite-type structure after being calcined at 950 oC for 5 h and the lattice constant decreased with the Pr content increasing.The electrical conductivity of Ba0.5Sr0.5Co0.8Fe0.2O3-δ(BSCF) was greatly enhanced by Pr-doping.The thermal expansion coefficient(TEC) of BSPCFx was increased with the content of Pr increasing,and all the thermal expansion curves had an inflection at about 250-400 oC due to the thermal-induced lattice oxygen loss and the reaction of Co and Fe ion.Ac impedance analysis indicated that BSPCFx possessed better electrochemical performance.The polarization resistance of the sample with x=0.2 was only ~0.948 Ω cm2 at 500 oC,significantly lower than that of BSCF(~2.488 Ω cm2).

详情信息展示

Preparation and performance of Pr-doped Ba0.5Sr0.5Co0.8Fe0.2O3-δ cathode for IT-SOFCs

朱成军,衣翠珊,潮洛蒙

Key Laboratory of Semiconductor Photovoltaic Technology of Inner Mongolia Autonomous Region,School of Physical Science and Technology,Inner Mongolia Univer-sity

摘 要:(Ba0.5Sr0.5)1-xPrxCo0.8Fe0.2O3-δ(BSPCFx;x=0.00-0.30) oxides were synthesized by a sol-gel thermolysis process using combination of PVA and urea,and were also investigated as cathode material for intermediate temperature solid oxide fuel cells(IT-SOFCs).X-ray diffraction(XRD) results showed that all the samples formed a single phase cubic pervoskite-type structure after being calcined at 950 oC for 5 h and the lattice constant decreased with the Pr content increasing.The electrical conductivity of Ba0.5Sr0.5Co0.8Fe0.2O3-δ(BSCF) was greatly enhanced by Pr-doping.The thermal expansion coefficient(TEC) of BSPCFx was increased with the content of Pr increasing,and all the thermal expansion curves had an inflection at about 250-400 oC due to the thermal-induced lattice oxygen loss and the reaction of Co and Fe ion.Ac impedance analysis indicated that BSPCFx possessed better electrochemical performance.The polarization resistance of the sample with x=0.2 was only ~0.948 Ω cm2 at 500 oC,significantly lower than that of BSCF(~2.488 Ω cm2).

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号