Development mechanism of internal local corrosion of X80 pipeline steel
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2020年第14期
论文作者：Zhuowei Tan Liuyang Yang Dalei Zhang Zhenbo Wang Frank Cheng Mingyang Zhang Youhai Jin
文章页码：186 - 201
摘 要：The occurrence and development mechanism of internal local corrosion has always been a controversial topic, and especially under flow conditions. In this paper, an improved high shear force loop was experimentally used, and local flow field is induced by simulating corrosion defects on the surface of X80 pipeline steel specimens. The characteristics of corrosion products deposited on the surface of specimens in CO2-saturated NACE solution were investigated by means of electrochemical impedance spectroscopy（EIS）, scanning electron microscopy（SEM）, X-ray diffraction（XRD）, and energy dispersive spectrometry（EDS）. The 3 D micromorphology of the corrosion test surface after remove the corrosion scale used to measure the size of localized corrosion pit. Under the influence of local defects, the wall shear stress（WSS） and turbulent kinetic energy of local flow fields enhanced significantly, and pressure fluctuations in local flow field were induced. The results showed that the characteristics of surface corrosion products varied with flow velocity. The corrosion scales formed in various regions of specimens with defects exhibited different surface micro-morphologies and chemical compositions. Overall, these data offer new perspectives for better understanding the mechanisms behind local corrosion.
Zhuowei Tan1，Liuyang Yang2，Dalei Zhang2，Zhenbo Wang1，Frank Cheng3，Mingyang Zhang4，Youhai Jin1
1. China University of Petroleum (East China)2. School of Materials Science and Engineering, China University of Petroleum (East China)3. University of Calgary4. School of Thermal Engineering, Shandong Jianzhu University
摘 要：The occurrence and development mechanism of internal local corrosion has always been a controversial topic, and especially under flow conditions. In this paper, an improved high shear force loop was experimentally used, and local flow field is induced by simulating corrosion defects on the surface of X80 pipeline steel specimens. The characteristics of corrosion products deposited on the surface of specimens in CO2-saturated NACE solution were investigated by means of electrochemical impedance spectroscopy（EIS）, scanning electron microscopy（SEM）, X-ray diffraction（XRD）, and energy dispersive spectrometry（EDS）. The 3 D micromorphology of the corrosion test surface after remove the corrosion scale used to measure the size of localized corrosion pit. Under the influence of local defects, the wall shear stress（WSS） and turbulent kinetic energy of local flow fields enhanced significantly, and pressure fluctuations in local flow field were induced. The results showed that the characteristics of surface corrosion products varied with flow velocity. The corrosion scales formed in various regions of specimens with defects exhibited different surface micro-morphologies and chemical compositions. Overall, these data offer new perspectives for better understanding the mechanisms behind local corrosion.
关键词：