Magnetic properties and crystallization kinetics of Zn0.5 Ni0.5 Fe2O4

来源期刊:Rare Metals2011年第6期

论文作者:WU Wenwei,CAI Jinchao,WU Xuehang,LI Yongni,and LIAO Sen School of Chemistry and Chemical Engineering,Guangxi University,Nanning ,P.R.China

文章页码:621 - 626

摘    要:Precursor of nanocrystalline Zn0.5Ni0.5Fe2O4 was obtained by grinding mixture of ZnSO4·7H2O,NiSO4·6H2O,FeSO4·7H2O,and Na2CO3·10H2O under the condition of surfactant polyethylene glycol(PEG)-400 being present at room temperature,washing the mixture with water to remove soluble inorganic salts and drying it at 373 K.The spinel Zn0.5Ni0.5Fe2O4 was obtained via calcining precursor above 773 K.The precursor and its calcined products were characterized by differential scanning calorimetry(DSC) ,Fourier transform infrared(FT-IR) ,X-ray diffraction(XRD) ,and vibrating sample magnetometer(VSM) .The result showed that Zn0.5Ni0.5Fe2O4 obtained at 1073 K had a saturation magnetization of 74 A·m2·kg-1.Kinetics of the crystallization process of Zn0.5Ni0.5Fe2O4 was studied using DSC technique,and kinetic parameters were determined by Kissinger equation and Moynihan et al.equation.The value of the activation energy associated with the crystallization process of Zn0.5Ni0.5Fe2O4 is 220.89 kJ·mol-1.The average value of the Avrami exponent,n,is equal to 1.59±0.13,which suggests that crystallization process of Zn0.5Ni0.5Fe2O4 is the random nucleation and growth of nuclei reaction.

详情信息展示

Magnetic properties and crystallization kinetics of Zn0.5 Ni0.5 Fe2O4

WU Wenwei,CAI Jinchao,WU Xuehang,LI Yongni,and LIAO Sen School of Chemistry and Chemical Engineering,Guangxi University,Nanning 530004,P.R.China

摘 要:Precursor of nanocrystalline Zn0.5Ni0.5Fe2O4 was obtained by grinding mixture of ZnSO4·7H2O,NiSO4·6H2O,FeSO4·7H2O,and Na2CO3·10H2O under the condition of surfactant polyethylene glycol(PEG)-400 being present at room temperature,washing the mixture with water to remove soluble inorganic salts and drying it at 373 K.The spinel Zn0.5Ni0.5Fe2O4 was obtained via calcining precursor above 773 K.The precursor and its calcined products were characterized by differential scanning calorimetry(DSC) ,Fourier transform infrared(FT-IR) ,X-ray diffraction(XRD) ,and vibrating sample magnetometer(VSM) .The result showed that Zn0.5Ni0.5Fe2O4 obtained at 1073 K had a saturation magnetization of 74 A·m2·kg-1.Kinetics of the crystallization process of Zn0.5Ni0.5Fe2O4 was studied using DSC technique,and kinetic parameters were determined by Kissinger equation and Moynihan et al.equation.The value of the activation energy associated with the crystallization process of Zn0.5Ni0.5Fe2O4 is 220.89 kJ·mol-1.The average value of the Avrami exponent,n,is equal to 1.59±0.13,which suggests that crystallization process of Zn0.5Ni0.5Fe2O4 is the random nucleation and growth of nuclei reaction.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号