Corrosion behaviour of NiCrFeAl-hBN seal coatings in oxidation environments at a high temperature

来源期刊：Rare Metals2021年第1期

论文作者：Su-Yuan Yang Dan Guo Xing-Wang Cheng Jian-Ming Liu Yue-Guang Yu

文章页码：212 - 218

摘要：The purpose of this investigation was to evaluate the microstructure,high-temperature oxidation behaviour,and hardness of a seal coating under controlled exposures at 750℃ with different exposure times.The results reveal that the main phases in the coating are Ni,FeNi₃,and hexagonal BN,with α-Al₂ O₃ peaks appearing after 2-h oxidation.As the exposure time increases,the diffraction peak intensity of α-Al₂ O₃ begins to decrease and Cr₂ O₃ peaks appear after 200 h.After 1000 h,Cr₂ O₃ becomes dominant with only small amounts of α-Al₂ O₃ remaining.The high-temperature oxidation process of the coating includes three stages:the fast stage,transition stage,and slow stage.The oxidation rate is constant in each stage,and in the fast stage and slow stages with values of7.9×10^-4 and 8.37×10^-5 mg2·cm^-4·s^-1,respectively.Initially,α-Al₂ O₃ forms near the pores in the coating,followed by the formation of Cr₂ O₃.As the exposure time increases,oxidation penetrates into the interior of the coating along phase boundaries to form island-shaped inner oxide layers with high concentrations of Cr,Ni,and Fe.Additionally,hardness increases with increasing oxide percentage.

稀有金属(英文版) 2021,40(01),212-218

Corrosion behaviour of NiCrFeAl-hBN seal coatings in oxidation environments at a high temperature

Su-Yuan Yang Dan Guo Xing-Wang Cheng Jian-Ming Liu Yue-Guang Yu

School of Materials Science and Engineering,Beijing Institute of Technology

National Key Laboratory of Science and Technology on Materials Under Shock and Impact

Beijing General Research Institute of Mining and Metallurgy

作者简介：Su-Yuan Yang e-mail:yangsuyuan@bit.edu.cn;

收稿日期：5 March 2019

基金：financially supported by the National Natural Science Foundation of China (No.51571031);

Corrosion behaviour of NiCrFeAl-hBN seal coatings in oxidation environments at a high temperature

Su-Yuan Yang Dan Guo Xing-Wang Cheng Jian-Ming Liu Yue-Guang Yu

School of Materials Science and Engineering,Beijing Institute of Technology

National Key Laboratory of Science and Technology on Materials Under Shock and Impact

Beijing General Research Institute of Mining and Metallurgy

Abstract：

The purpose of this investigation was to evaluate the microstructure,high-temperature oxidation behaviour,and hardness of a seal coating under controlled exposures at 750℃ with different exposure times.The results reveal that the main phases in the coating are Ni,FeNi₃,and hexagonal BN,with α-Al₂ O₃ peaks appearing after 2-h oxidation.As the exposure time increases,the diffraction peak intensity of α-Al₂ O₃ begins to decrease and Cr₂ O₃ peaks appear after 200 h.After 1000 h,Cr₂ O₃ becomes dominant with only small amounts of α-Al₂ O₃ remaining.The high-temperature oxidation process of the coating includes three stages:the fast stage,transition stage,and slow stage.The oxidation rate is constant in each stage,and in the fast stage and slow stages with values of7.9×10^-4 and 8.37×10^-5 mg2·cm^-4·s^-1,respectively.Initially,α-Al₂ O₃ forms near the pores in the coating,followed by the formation of Cr₂ O₃.As the exposure time increases,oxidation penetrates into the interior of the coating along phase boundaries to form island-shaped inner oxide layers with high concentrations of Cr,Ni,and Fe.Additionally,hardness increases with increasing oxide percentage.

Keyword：

NiCrFeAl-hBN; Seal coating; Oxidation; Microstructure; High temperature;

Received： 5 March 2019

1 Introduction

With the rapid development in the aviation industry,large propulsive force,high efficiency,and low fuel consumption have become the main objectives of the design and manufacture of aircraft engines [ 1, 2] .However,the gap between engine blades and the engine casing is an important factor that reduces the overall efficiency of an engine and increases fuel consumption [ 3, 4] .Based on various factors,such as thermal expansion of the engine assembly and elongation of the blades caused by high-speed rotational centrifugal force,this gap cannot be controlled to zero [ 5, 6] .Therefore,abradable seal coatings are deposited onto the shrouds aircraft engines using thermal spray technology to minimize blade-tip clearances and enhance the efficiency of engines.Such coatings have many advantages,such as simple manufacturing processes,easy to repair,adjustable properties,and good sealing effectiveness [ 7] .Abradable seal coatings operate in highly demanding environments and are required to exhibit certain properties,including abradability,corrosion resistance,hightemperature stability,erosion resistance,and sufficient bond strength with the underlying material [ 8, 9, 10] .To meet this complex combination of requirements,such coatings are largely composed of metal phases (e.g.,Ni,Cu,Al,and various alloys) and self-lubricating non-metal phases (e.g.,graphite,hBN diatomite,and high molecular polymers) with high porosity [ 11] .Metal phases provide high strength,oxidation resistance,and hot-corrosion resistance.Self-lubricating nonmetal phases mainly provide lubrication for coatings and enhance porosity to reduce the hardness of coatings [ 12, 13] .

The structures and properties of thermally sprayed coatings depend heavily on their level of oxidation,which is one of the key characteristics of such coatings.The working environment of a seal coating is a high-temperature oxidation atmosphere and oxidation is one of the main failure modes of such coatings.Therefore,it is important to study the micros true ture changes in seal coatings after exposure to a high temperature to research this failure process and improve service life [ 14, 15, 16, 17] .

However,most previous studies have focused on other properties,such as abradability and anti-erosion ability [ 18, 19, 20, 21, 22] ,meaning fundamental investigations of microstructure and thermal properties are still lacking [ 23, 24] .In this study,the microstructure and high-temperature oxidation behaviours of a NiCrFeAl-hBN seal coating were investigated at 750℃with various exposure times.

2 Experimental

The seal coating system studied in this work (Fig.la)consists of a GH4169 substrate,APS-deposited NiCrAl bond coating,and NiCrFeAl-hBN top coating (～1.5 mm in thickness) that was applied using a flame spray process(Table 1).The feedstock powders for the top coating were supplied by Beijing General Research Institute of Mining and Metallurgy (China).Their chemical compositions are listed in Table 2.The size of the top coating powders was relatively uniform,as shown in Fig.1b.The NiCrAl powders were pre-sprayed onto the surface of the GH4169substrate to a thickness of～60μm to improve the adhesive bond strength of the seal coating.

The coated specimens were treated at 750℃in an ambient atmosphere with exposure times of 2,6,40,80,200,and 1000 h,and then cooled in open air.The oxidized samples were subjected to a discontinuous weighing method.Specifically,after a certain period of oxidation,the samples were cooled and weighed,then returned to the furnace for further oxidation,then cooled and weighed again.The samples were weighed by an electronic balance with an accuracy of 0.1 mg.

下载原图

Table 1 Process parameters of flame spraying

下载原图

Table 2 Chemical composition of powders of NiCrFeAl-hBN top coating (wt%)

The microstructures of the NiCrFeAl-hBN coatings were investigated before and after high-temperature oxidation by means of scanning electron microscopy (SEM,FEI QUANTA 600) equipped with energy-dispersive spectroscopy (EDS),electron probe micro-analysis(EPMA,JXA-8230) compositional mapping,and X-ray diffraction (XRD,D8 advance) using a Cu Koc radiation source.The volumetric porosity and oxide percentage of the top coat were determined by using an image analysis technique with the aid of the ImageJ software package.Hardness measurements were carried out for all specimens by using an HR15Y device (MODEL 600 MRD-S).

3 Results and discussion

3.1 Phase analysis

XRD patterns of the coatings treated at 750℃for 0,2,200,and 1000 h are presented in Fig.2.The main phases in the untreated coating were Ni,FeNi₃ and hexagonal BN.After 2-h exposure at 750℃,α-Al₂O₃ peaks appeared in the diffraction pattern,indicating that the oxidation of aluminium occurred during the exposure process.As the exposure time increased,the diffraction peak intensity ofα-Al₂O₃ began to decrease and Cr₂O₃ peaks appeared after200 h.After 1000 h,the oxide phase of Cr₂O₃ became dominant,with only a small amount of a-Al₂O₃ remaining.

Fig.1 SEM images of a abradable seal coating and b powders

3.2 Microstructure

SEM microstructures of the coatings exposed at 750℃for different exposure times are presented in Fig.3.The coatings are largely composed of hBN phases (dark grey)of varying size,metal matrices (white),and oxides (light grey) with significant levels of porosity (black).The chemical compositions of these regions were determined via EDS.

Fig.2 XRD patterns of NiCrFeAl-hBN coatings after exposure for different times at 750^°C

A summary of the compositional data of the points shown in Fig.3 is provided in Table 3.The main elements in the light grey area are Al (exposure time>2 h) and Cr(exposure time>6 h).This result is supported by XRD results (Fig.2).After heat treatment for 2 and 6 h (Fig.3a,b,respectively),the oxides were largely composed ofα-Al₂O₃,When the heat treatment time was 40 and 80 h(Fig.3c,d,respectively),the oxides wereα-Al₂O₃ and Cr₂O_3.When comparing SEM images of these two oxides,the image of a-Al₂O₃ was found to be smoother than that of Cr₂O₃,as shown in Fig.3c.After 200 h (Fig.3e,f),Ni and Fe began to oxidize,but only to a small degree,so Fig.2does not show any peaks for these oxides.The oxides mainly appeared near the pores in the coating when the exposure time was short.After 200 h (Fig.3f),oxides formed in the metal matrices.The oxides of Ni and Fe in the coating after 1000 h were more prominent than those in the coating after 200 h.

EPMA elemental mapping graphs for the NiCrFeAlhBN coating after 2-and 1000-h oxidation at 750℃are presented in Figs.4 and 5,respectively.It is difficult to observe the existence of hBN using XRD or SEM due to its low content,but EPMA proves the existence of hBN.Although the content of hBN is low,its distribution is uniform (Figs.4e and 5e),which ensures the abradability of the coating.Ni is the most abundant metallic element in the coating and mainly exists in metal matrices surrounded by Cr (Figs.4b and 5b).As shown in Figs.4d and 5d,Al mainly exists in the grey area around the pores (dark area).As shown by the results of XRD and SEM,it mainly exists in the form of a-Al₂O_3.Cr is well distributed in the metal matrices after 2-h oxidation (Fig.4c).After 1000 h,it largely exists aroundα-Al₂O₃ in the form of Cr₂O_3.Additionally,visible segregation of Cr in the metal matrices of the coating appears after 1000 h (Fig.5c),which is considered to be the result of the long exposure time at750℃ [ 25] .

Fig.3 SEM images of NiCrFeAl-hBN coatings after different exposure times at 750℃:a 2 h,b 6 h,c 40 h,d 80 h,e 200 h,and f 1000 h

下载原图

Table 3 Summary of EDS results for areas in Fig.3 (at%)

3.3 Porosity and oxide percentage

Figure 6 presents the changes in porosity and oxide content of the seal coatings with various exposure times at 750℃.The porosity of the coating is approximately 23.5%without any heat treatment.This value decreases with prolonged exposure time,reaching 11.75%after 1000 h.The rate of decrease is rapid initially and then slows after 200 h.The oxide content in the coating increases with exposure time increasing.The main reason for the decrease in porosity over time is the change in the oxide percentage.

3.4 Oxidation kinetics

The oxidation weight change per unit area (mg·cm^-2) of the NiCrFeAl-hBN coating with heat treatment at 750℃is presented in Fig.7a.The oxidation weight change of the coating exhibits three main stages:the fast oxidation stage(0-30 h),transition stage,and slow oxidation stage (after60 h).Figure 7b presents the square of the weight gain per unit area of the NiCrFeAl-hBN coating versus time.The fast and slow oxidation stages conform to the parabolic law,meaning that the oxidation dynamic parabola constant can be used to evaluate the oxidation rate.The oxidation rate constant (K_p,parabolic rate constant) was calculated by using a linear least-square function:

Fig.4 EPMA elemental mapping graphs for NiCrFeAl-hBN coating treated after 2 h at 750℃a cp,b Ni,c Cr,d Al,and e B

Fig.5 EPMA elemental mapping graphs for NiCrFeAl-hBN coating treated after 1000 h at 750℃a cp,b Ni,c Cr,d Al,and e B

Fig.6 Curves of porosity and oxide percentage of coating versus exposure time at 750℃

where (ΔW/A) is the weight gain per unit area and t is the oxidation time in seconds [ 26] .The parabolic rate constants for the NiCrFeAl-hBN coating in the fast and slow oxidation stages are 7.59×10^-4 and 8.37×10^-5 mg²·cm^-4·s^-1,respectively.The oxidation rate in the fast oxidation stage is an order of magnitude greater than that in the slow oxidation stage.Additionally,the oxidation rate constant in the fast oxidation stage is approximately three orders of magnitude smaller than that of the substrate metal (GH4169),meaning that the NiCrFeAl-hBN coating successfully protects the substrate at high temperatures [ 27] .

The metal elements in the coating largely consist of Ni,Cr,Fe,and Al,which can be oxidized into NiO,Cr₂O₃,FeO,Fe₂O₃,Fe₃O₄,and Al₂O₃ at 750℃in air.The formula for Gibbs free energy (AG_T) is shown in Eq.(2).

where AG₀ is the change in metal oxidation free energy in the standard state (T=298.15 K,p=101.3 kPa,R=8.314 J·mol^-1·K^-1),and a is the activity of the inpidual components.

When comparing the Gibbs free energies of the oxidized metal elements in the coating,we find thatΔGAl2O3<<ΔG_FeO<ΔG_Fe3O₄<ΔG_Fe2O₃<ΔGNiO.Therefore,Al is oxidized preferentially near the pores in the coating,followed by Cr.The high stability of these elements means that the Ni and Fe in the coating can be prevented from oxidizing during heat treatment.Furthermore,even if Ni and Fe are oxidized in the presence of A1 and Cr,the oxides of Ni and Fe will become unstable and decompose back into Ni and Fe [ 28] .This is why no oxidation of Ni and Fe occurred in the coatings with short exposure time,as shown in Figs.2 and 3.After 200 h,based on the limited concentration of free Al and Cr,Ni and Fe begin to oxidize in the metal matrices.However,the peaks of Ni and Fe oxides cannot be observed in the XRD results,indicating low concentrations of these oxides.

Fig.7 a Oxidation kinetics curve of NiCrFeAl-hBN coating at 750℃;b relationship between square of weight gain and time of NiCrFeAl-hBN coating at 750℃

With a further increase in the exposure time,additional oxygen ions diffuse into the interior of the coating through pores.Based on the large amount of defects at grain boundaries,high oxygen concentrations and low aluminium concentrations form deficient Al₂O₃ to prevent further oxidation.However,oxidation develops in the interior of the coating along grain boundaries or phase boundaries to form island-shaped inner oxide layers.The formation and development of oxides along boundaries lead to the diffusion of Cr in the matrices into oxides,which reduces the concentration of Cr in the matrices [ 29] .This results in an uneven composition,and the inner oxide layer is enriched by higher Cr concentrations(Fig.5c).

The weight gains of the coatings at 750℃exhibit three stages because of the formation of oxides in the NiCrFeAlhBN coating,as described above.In the fast oxidation stage,the main oxidation in the coating is the formation of Al₂O_3.Next,Cr₂O₃ appears and oxides form around pores,where the chance to bond with oxygen atoms is sufficient.Based on the protection of these oxides,with oxidation time increasing,oxidation develops in the interior of the coating along grain boundaries or phase boundaries,where the chance of metal elements attaching to oxygen atoms is lower than that in the pores.The oxidation rate then slows and the process passes through the transition stage before reaching the slow oxidation stage.The growth rate of each oxide obeys parabolic kinetics,resulting in parabolic oxidation kinetics for the coating in each stage of oxidation [ 30, 31, 32] .

Fig.8 Curve of hardness of coatings versus exposure time at 750℃

3.5 Hardness

Figure 8 presents the change in the hardness of NiCrFeAlhBN seal coatings with various exposure time at 750℃.One can see that the hardness increases as the heat treatment time increases.Furthermore,the rate of increase is rapid initially and then slows after 200 h.This phenomenon can be explained by the following reasons.First,the formation of oxides increases hardness because the hardness values of metal oxides,such as alumina and chromium oxide,are greater than those of the base metals.Second,previous studies have shown that the hardness of seal coatings can be affected by the changes in porosity [ 3, 8] .

4 Conclusions

The microsttuctures and high-temperature corrosion behaviours of coatings under controlled exposure at 750℃with exposure time of 2,6,40,80,200,and 1000 h were investigated.The main results are as follows.The coating microstructure is composed of FeNi₃,Ni,and hBN.The high-temperature oxidation process includes three stages:the fast stage,transition stage,and slow stage.α-Al₂O₃peaks appear after 2-h exposure.As exposure time increases,the diffraction peak intensity ofα-Al₂O₃ begins to decrease and Cr₂O₃ peaks appear after 200 h.After1000 h,Cr₂O₃ becomes dominant with a small amount of remaining a-Al₂O_3.The main oxides of a-Al₂O₃ and Cr₂O₃are formed around the pores in the coating initially.The inner oxide layer is enriched with higher concentrations of Cr,Ni,and Fe after 200 h.Finally,the hardness of the coating increases with exposure time increasing.