来源期刊:中国有色金属学报1998年第1期

论文作者:席生岐 屈晓燕 郑修麟 马明亮 周敬恩 王笑天

文章页码:43 - 46

关键词:高能球磨 固态反应 Al/CuO反应

Key words:solid state reaction , Al/CuO reaction , high energy ball milling

摘    要:系统研究了Al/CuO的高能球磨固态反应。对Al含量在20%~85%范围内的Al/CuO进行高能球磨, 采用X射线衍射进行物相分析, 并对Al含量分别为20% 和75%的试验分析了物相随研磨时间的变化,做了差示扫描量热(DSC)分析,对比研究了固态还原反应与固态复合反应过程的异同。结果表明,Al含量不超过20%时仅发生单纯的还原反应;当Al含量从20%分别增加到35%,57%,70%和85%时,反应为还原与合成共存的复合反应,产物依次为Cu9Al4,CuAl2及Al(Cu)固溶体和Al2O3的复合颗粒。

Abstract: The solid state reaction of Al/CuO induced by high energy stirring ball milling was studied systematically. Chemically pure elemental Al and CuO powder with an Al mass percentage of 20, 35, 57, 70 and 85 were milled respectively. The ball milled powders were analyzed by X-ray diffractometry(XRD ) and differential scanning calorimetry (DSC). When the amount of Al was under 20%, the reduction occurred only. When the amount of Al exceeded 20%, besides reduction, the synthesis reaction occurred simultaneously. The composite reaction existed in this reaction couple. As the amount of Al increased, the products were Cu9Al4, CuAl2 and Al(Cu) solution + Al2O3 respectively. The mechanisms of these two types of reaction during ball milling were discussed.

详情信息展示

 

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号