Effect of Rotation Rate on Microstructure and Mechanical Properties of Friction Stir Spot Welded DP780 Steel

来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2016年第4期

论文作者:G.M.Xie H.B.Cui Z.A.Luo W.Yu J.Ma G.D.Wang

文章页码:326 - 332

摘    要:DP780 steel sheets consisting of ferrite and martensite were successfully friction stir spot welded(FSSW)at the rotation rates of 500 to 1500 r/min using a W-Re alloy tool.The effect of rotation rate on microstructure and mechanical properties of the FSSW DP780 was investigated.The peak temperatures in the welds at various rotation rates were identified to be above A3temperature.FSSW caused the dynamic recrystallization in the stir zone(SZ),thereby producing the fine equiaxed grain structures.At the higher rotation rates of≥1000 r/min,a full martensitic structure was observed throughout the SZs,whereas at the lower rotation rate of 500 r/min,the SZ consisted of a fine dual phase structure of ferrite and martensite due to the action of deformation induced ferrite transformation.The maximum average failure load as high as 18.2 k N was obtained at the rotation rate of 1000 r/min and the fracture occurred at the thinned upper sheet.

详情信息展示

Effect of Rotation Rate on Microstructure and Mechanical Properties of Friction Stir Spot Welded DP780 Steel

G.M.Xie,H.B.Cui,Z.A.Luo,W.Yu,J.Ma,G.D.Wang

State Key Laboratory of Rolling and Automation, Northeastern University

摘 要:DP780 steel sheets consisting of ferrite and martensite were successfully friction stir spot welded(FSSW)at the rotation rates of 500 to 1500 r/min using a W-Re alloy tool.The effect of rotation rate on microstructure and mechanical properties of the FSSW DP780 was investigated.The peak temperatures in the welds at various rotation rates were identified to be above A3temperature.FSSW caused the dynamic recrystallization in the stir zone(SZ),thereby producing the fine equiaxed grain structures.At the higher rotation rates of≥1000 r/min,a full martensitic structure was observed throughout the SZs,whereas at the lower rotation rate of 500 r/min,the SZ consisted of a fine dual phase structure of ferrite and martensite due to the action of deformation induced ferrite transformation.The maximum average failure load as high as 18.2 k N was obtained at the rotation rate of 1000 r/min and the fracture occurred at the thinned upper sheet.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号