论文作者：Hui-ping Shao Xiao-ting Liu Ye Ji Zhi-meng Guo
文章页码：1076 - 1080
摘 要：Spherical Ti-45Al-8.5Nb-（W,B,Y）alloy powder prepared by an argon plasma process was near-net shape by gelcasting.In the non-aqueous system,methaerylate-2-hydroxy ethyl,toluene,benzoyl peroxide,and N,N-dimethylaniline were used as the monomer,solvent,initiator,and catalyst,respectively.To improve sintering and forming behaviors,many additives were included in the suspension.The concentrated suspension with a solid loading of 70vol%was prepared.The high Nb-TiAl powder was analyzed by electron microscopy and X-ray difraction.It was found that the green bodies had a smooth surface and homogeneous microstructure,exhibiting a bending strength as high as 50 MPa.After sintering at1480 C for 2 h in vacuum,uniform complex-shaped high Nb-TiAl parts were successfully produced.
Hui-ping Shao，Xiao-ting Liu，Ye Ji，Zhi-meng Guo
Institute for Advanced Material & Technology,University of Science and Technology Beijing
摘 要：Spherical Ti-45Al-8.5Nb-（W,B,Y）alloy powder prepared by an argon plasma process was near-net shape by gelcasting.In the non-aqueous system,methaerylate-2-hydroxy ethyl,toluene,benzoyl peroxide,and N,N-dimethylaniline were used as the monomer,solvent,initiator,and catalyst,respectively.To improve sintering and forming behaviors,many additives were included in the suspension.The concentrated suspension with a solid loading of 70vol%was prepared.The high Nb-TiAl powder was analyzed by electron microscopy and X-ray difraction.It was found that the green bodies had a smooth surface and homogeneous microstructure,exhibiting a bending strength as high as 50 MPa.After sintering at1480 C for 2 h in vacuum,uniform complex-shaped high Nb-TiAl parts were successfully produced.
关键词：