应用COMI炼钢工艺控制转炉烟尘基础研究
来源期刊：钢铁2009年第10期
论文作者：尹振江 朱荣 易操 陈伯瑜 汪灿荣 柯建祥
文章页码：92 - 94
关键词：转炉烟尘； CO2； 分时段
Key words：converter dust； CO2； divided-period
摘 要：应用COMI炼钢工艺控制转炉烟尘实验研究表明,随着CO2喷吹比例的增加,烟尘及铁损量持续降低。转炉烟尘现场采集检测试验研究表明,转炉冶炼过程中烟尘量总体趋势不断降低,TFe含量波动较大。结合上述研究,提出应用COMI炼钢工艺分时段控制烟尘产生,为COMI炼钢工艺的工业实施提供了参考。
Abstract: By applying COMI converter steel-making process control dust,the results show that increasing the proportion of CO2 injection,converter dust and amount of iron loss are continued to decrease.And the research on converter dust collected on-site test showed that the overall amount of converter dust are continued to trend lower in the process,TFe content had the larger fluctuation.Combination of the above-mentioned study,it is proposed that application of COMI steel-making process to control the generation of converter dust is divided-period,which provides a reference for the industry implementation of the COMI steel-making process.
尹振江1,2，朱荣1，易操2，陈伯瑜3，汪灿荣3，柯建祥3
(1.北京市北京科技大学 冶金与生态工程学院
2.江西省南昌市南昌长力钢铁股份有限公司
3.福建三钢闽光股份有限公司，福建三明 365000)
摘 要：应用COMI炼钢工艺控制转炉烟尘实验研究表明,随着CO2喷吹比例的增加,烟尘及铁损量持续降低。转炉烟尘现场采集检测试验研究表明,转炉冶炼过程中烟尘量总体趋势不断降低,TFe含量波动较大。结合上述研究,提出应用COMI炼钢工艺分时段控制烟尘产生,为COMI炼钢工艺的工业实施提供了参考。
关键词：转炉烟尘； CO2； 分时段