Microwave Sintering of Al2O3-ZrO2-WC-Co Cermets
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第2期
论文作者：谷天本 陆洪智
文章页码：290 - 292
摘 要：Composite powders of nanocrystalline WC-10Co （15wt%）,Y2O3 （8mol%） stabilized nanocrystalline ZrO2 （30wt%）,industrial cobalt powder （4.5wt%） and submicron Al2O3 （55wt%） composite powders were fabricated by high-energy ball-milling process.The nanocomposite powders were consolidated by microwave sintering process at temperature ranged 1300℃-1550℃ for 15min,respectively.The optimum consolidation conditions,such as temperature,were researched during microwave sintering process.Vickers Hardness of the consolidated cermets was measured by using a Vickers indentation test,and density of specimens was also determined by Archimedes’ principle.Microwave sintering process could not only increase the density of Al2O3-ZrO2-WC-Co cermets and reduce the porosity,but also inhibit abnormal grain growth.
谷天本1，陆洪智2
1. Faculty of Engineering,China University of Geosciences2. Third Geological Prospecting Team,Henan Geology and Mineral Bureau,Luoyang 471023,China
摘 要：Composite powders of nanocrystalline WC-10Co （15wt%）,Y2O3 （8mol%） stabilized nanocrystalline ZrO2 （30wt%）,industrial cobalt powder （4.5wt%） and submicron Al2O3 （55wt%） composite powders were fabricated by high-energy ball-milling process.The nanocomposite powders were consolidated by microwave sintering process at temperature ranged 1300℃-1550℃ for 15min,respectively.The optimum consolidation conditions,such as temperature,were researched during microwave sintering process.Vickers Hardness of the consolidated cermets was measured by using a Vickers indentation test,and density of specimens was also determined by Archimedes’ principle.Microwave sintering process could not only increase the density of Al2O3-ZrO2-WC-Co cermets and reduce the porosity,but also inhibit abnormal grain growth.
关键词：