Effects of samarium addition on as-cast microstructure, grain refinement and mechanical properties of Mg-6Zn-0.4Zr magnesium alloy
来源期刊：JOURNAL OF RARE EARTHS2017年第5期
论文作者：张玉 黄晓锋 李雅 马振铎 马颖 郝远
文章页码：494 - 502
摘 要：In this paper, the microstructural evolution, grain refinement and mechanical properties of as-cast Mg-6Zn-0.4Zr alloys with varying Sm contents（0, 2 wt.%, 4 wt.% and 6 wt.%） were investigated by using an optical microscope（OM）, a scanning electron microscope（SEM） equipped with energy dispersive spectroscope（EDS）, an X-ray diffractometer（XRD） and mechanical tests at room temperature, respectively. The experimental results indicated that the addition of Sm could obviously refine the as-cast grains, modify the eutectic morphology and affect the mechanical properties of the alloys. The main phases in Mg-6Zn-xSm-0.4Zr alloys included matrix α-Mg, Mg2Zn3, Mg41Sm5 and MgZ nS m. With Sm content increasing to 4%, the MgZ nS m phase was created, meanwhile, the morphology of some eutectic phases revealed apparently lamellar structure, which had a bad effect on the mechanical properties. In addition, the maximum values of ultimate tensile strength（UTS, 214 MPa） and elongation（EL, 7.42%） were simultaneously obtained from the alloy with 2% Sm. However, Sm addition had no obvious effects on the fracture behavior of the alloys, namely, the fracture pattern of Mg-6Zn-0.4Zr alloy belonged to inter-granular and brittle modes while the fracture regimes of all the Sm-containing alloys were dominated by the mixture of inter-granular and trans-granular modes.
张玉，黄晓锋，李雅，马振铎，马颖，郝远
State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology
摘 要：In this paper, the microstructural evolution, grain refinement and mechanical properties of as-cast Mg-6Zn-0.4Zr alloys with varying Sm contents（0, 2 wt.%, 4 wt.% and 6 wt.%） were investigated by using an optical microscope（OM）, a scanning electron microscope（SEM） equipped with energy dispersive spectroscope（EDS）, an X-ray diffractometer（XRD） and mechanical tests at room temperature, respectively. The experimental results indicated that the addition of Sm could obviously refine the as-cast grains, modify the eutectic morphology and affect the mechanical properties of the alloys. The main phases in Mg-6Zn-xSm-0.4Zr alloys included matrix α-Mg, Mg2Zn3, Mg41Sm5 and MgZ nS m. With Sm content increasing to 4%, the MgZ nS m phase was created, meanwhile, the morphology of some eutectic phases revealed apparently lamellar structure, which had a bad effect on the mechanical properties. In addition, the maximum values of ultimate tensile strength（UTS, 214 MPa） and elongation（EL, 7.42%） were simultaneously obtained from the alloy with 2% Sm. However, Sm addition had no obvious effects on the fracture behavior of the alloys, namely, the fracture pattern of Mg-6Zn-0.4Zr alloy belonged to inter-granular and brittle modes while the fracture regimes of all the Sm-containing alloys were dominated by the mixture of inter-granular and trans-granular modes.
关键词：