Utilization of Red Mud as Raw Material in the Production of Field Road Cement

来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2016年第4期

论文作者:王晓 LUO Zhongtao ZHANG Lei RONG Hui YANG Jiujun

文章页码:877 - 882

摘    要:The total utilization amount of red mud is limited due to its high content of alkali,heavy metals and naturally occurring radioactive element.In order to rationalize the use of red mud,a typical field road cement using dealkalized red mud(content of alkali lower than 1%) as raw material was firstly prepared in this paper.Then,a preliminary research on the radioactivity of the red mud based field road cement has been carried out.For that reason,two samples of raw materials were prepared.One was with ordinary raw materials,as the control group(CG),the other was with 23 w % red mud,as the experimental group(EG).The clinkers were acquired by sintering the above two raw materials at 1 400 ℃.Subsequently,the two types of cement prepared by the above two kinds of clinkers were tested by measuring the normal consistency,setting time,mechanical strength and drying shrinkage.Meanwhile,the hydration products of the two types of cement were examined by XRD analysis at the curing age of 6 hours,1,3,7,and 28 days,respectively.The radioactivity of the two kinds of cement clinkers was then measured by gamma-ray spectrometry.The experimental results indicate that the main mineralogical phases components in the EG field road cement clinkers are C3S,C2S,and C4AF,the 28 days flexural and compressive strength of the EG field road cement mortars could be up to 8.45 and 53.2 MPa,respectively.The radioactive measuring results of the EG field road cement show that the value of radium equivalent activity index(Raeq) is 254.8 Bq/Kg-1,which is lower than the upper limit.

详情信息展示

Utilization of Red Mud as Raw Material in the Production of Field Road Cement

王晓1,LUO Zhongtao1,ZHANG Lei2,RONG Hui2,YANG Jiujun1,2

1. School of Materials Science and Engineering,Zhengzhou University2. School of Materials Science and Engineering,Tianjin Chengjian University

摘 要:The total utilization amount of red mud is limited due to its high content of alkali,heavy metals and naturally occurring radioactive element.In order to rationalize the use of red mud,a typical field road cement using dealkalized red mud(content of alkali lower than 1%) as raw material was firstly prepared in this paper.Then,a preliminary research on the radioactivity of the red mud based field road cement has been carried out.For that reason,two samples of raw materials were prepared.One was with ordinary raw materials,as the control group(CG),the other was with 23 w % red mud,as the experimental group(EG).The clinkers were acquired by sintering the above two raw materials at 1 400 ℃.Subsequently,the two types of cement prepared by the above two kinds of clinkers were tested by measuring the normal consistency,setting time,mechanical strength and drying shrinkage.Meanwhile,the hydration products of the two types of cement were examined by XRD analysis at the curing age of 6 hours,1,3,7,and 28 days,respectively.The radioactivity of the two kinds of cement clinkers was then measured by gamma-ray spectrometry.The experimental results indicate that the main mineralogical phases components in the EG field road cement clinkers are C3S,C2S,and C4AF,the 28 days flexural and compressive strength of the EG field road cement mortars could be up to 8.45 and 53.2 MPa,respectively.The radioactive measuring results of the EG field road cement show that the value of radium equivalent activity index(Raeq) is 254.8 Bq/Kg-1,which is lower than the upper limit.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号