Preparation of lanthanum sulfide nanoparticles by thermal decomposition of lanthanum complex
来源期刊：Journal of Rare Earths2011年第4期
论文作者：李培森 李焕勇 介万奇
文章页码：317 - 320
摘 要：γ-La2S3 nanoparticles were successfully prepared by thermal decomposition of lanthanum complex La（Et2S2CN）3·phen at low temperature. The obtained sample was characterized by the X-ray powder diffraction （XRD）, scanning electron microscopy （SEM） and element analysis. The decomposition mechanism of lanthanum complex was studied by thermogravimetric analyses （TGA）. The results showed that the obtained samples were cubic phase particles with uniform sizes among 10-30 nm and γ-La2S3 was prepared by decomposition of La（Et2S2CN）3·phen via La4（Et2S2CN）3 as an intermediate product. The band gap of γ-La2S3 was 2.97 eV, which was bigger than bulk crystal because of pronounced quantum confinement effect.
李培森，李焕勇，介万奇
School of Materials Science and Engineering, Northwestern Polytechnical University
摘 要：γ-La2S3 nanoparticles were successfully prepared by thermal decomposition of lanthanum complex La（Et2S2CN）3·phen at low temperature. The obtained sample was characterized by the X-ray powder diffraction （XRD）, scanning electron microscopy （SEM） and element analysis. The decomposition mechanism of lanthanum complex was studied by thermogravimetric analyses （TGA）. The results showed that the obtained samples were cubic phase particles with uniform sizes among 10-30 nm and γ-La2S3 was prepared by decomposition of La（Et2S2CN）3·phen via La4（Et2S2CN）3 as an intermediate product. The band gap of γ-La2S3 was 2.97 eV, which was bigger than bulk crystal because of pronounced quantum confinement effect.
关键词：