Preparation and properties of Nd:YAG ultra-fine powders
来源期刊:Journal of Rare Earths2011年第1期
论文作者:陈娇 黄啸谷 王丽熙 张其土
文章页码:44 - 47
摘 要:Ultra-fine Nd:YAG powders with different doping concentrations were synthesized by sol-gel combustion method.The pure Nd:YAG could be prepared at the low temperature of 900 oC.Ethanol could improve the dispersity of powders,and the average size of the ul-tra-fine powders was around 250 nm.The reflection spectrum showed that there were several apparent characteristic absorption peaks and the intensity of these peaks enhanced with the increasing concentration of Nd3+.The luminescence spectrum,which was excited by 808 nm wavelength,exhibited several obvious emission bands in the range of 900–1150 nm.The emission intensity of Nd:YAG powders increased until the Nd content was above 3 mol.% due to the fluorescent quenching effect.
陈娇1,黄啸谷1,王丽熙1,张其土1,2
1. College of Materials Science and Engineering,Nanjing University of Technology2. Jiangsu Provincial Key Laboratory of New Materials of Inorganic and Its Composites,Nanjing University of Technology
摘 要:Ultra-fine Nd:YAG powders with different doping concentrations were synthesized by sol-gel combustion method.The pure Nd:YAG could be prepared at the low temperature of 900 oC.Ethanol could improve the dispersity of powders,and the average size of the ul-tra-fine powders was around 250 nm.The reflection spectrum showed that there were several apparent characteristic absorption peaks and the intensity of these peaks enhanced with the increasing concentration of Nd3+.The luminescence spectrum,which was excited by 808 nm wavelength,exhibited several obvious emission bands in the range of 900–1150 nm.The emission intensity of Nd:YAG powders increased until the Nd content was above 3 mol.% due to the fluorescent quenching effect.
关键词: