Effect of Fe2O3 on the crystallization behavior of glass-ceramics produced from naturally cooled yellow phosphorus furnace slag

来源期刊:International Journal of Minerals Metallurgy and Materials2017年第3期

论文作者:Hong-pan Liu Xiao-feng Huang Li-ping Ma Dan-li Chen Zhi-biao Shang Ming Jiang

文章页码:316 - 323

摘    要:CaO–Al2O3–SiO2(CAS) glass-ceramics were prepared via a melting method using naturally cooled yellow phosphorus furnace slag as the main raw material.The effects of the addition of Fe2O3 on the crystallization behavior and properties of the prepared glass-ceramics were studied by differential thermal analysis,X-ray diffraction,and scanning electron microscopy.The crystallization activation energy was calculated using the modified Johnson–Mehl–Avrami equation.The results show that the intrinsic nucleating agent in the yellow phosphorus furnace slag could effectively promote the crystallization of CAS.The crystallization activation energy first increased and then decreased with increasing amount of added Fe2O3.At 4wt% of added Fe2O3,the crystallization activation energy reached a maximum of 676.374 k J×mol-1.The type of the main crystalline phase did not change with the amount of added Fe2O3.The primary and secondary crystalline phases were identified as wollastonite(CaSiO3) and hedenbergite(Ca Fe(Si2O6)),respectively.

详情信息展示

Effect of Fe2O3 on the crystallization behavior of glass-ceramics produced from naturally cooled yellow phosphorus furnace slag

Hong-pan Liu1,Xiao-feng Huang1,Li-ping Ma1,Dan-li Chen1,Zhi-biao Shang1,Ming Jiang1,2

1. Faculty of Environmental Science and Engineering,Kunming University of Science and Technology2. College of Resources and Environment,Yunnan Agricultural University

摘 要:CaO–Al2O3–SiO2(CAS) glass-ceramics were prepared via a melting method using naturally cooled yellow phosphorus furnace slag as the main raw material.The effects of the addition of Fe2O3 on the crystallization behavior and properties of the prepared glass-ceramics were studied by differential thermal analysis,X-ray diffraction,and scanning electron microscopy.The crystallization activation energy was calculated using the modified Johnson–Mehl–Avrami equation.The results show that the intrinsic nucleating agent in the yellow phosphorus furnace slag could effectively promote the crystallization of CAS.The crystallization activation energy first increased and then decreased with increasing amount of added Fe2O3.At 4wt% of added Fe2O3,the crystallization activation energy reached a maximum of 676.374 k J×mol-1.The type of the main crystalline phase did not change with the amount of added Fe2O3.The primary and secondary crystalline phases were identified as wollastonite(CaSiO3) and hedenbergite(Ca Fe(Si2O6)),respectively.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号