Effect of Yb2O3 additives on structure and transport properties of YBa2Cu3O7-δ
来源期刊：JOURNAL OF RARE EARTHS2010年第S1期
论文作者：徐胜 虞爱平 顾艳妮 吴小山
文章页码：434 - 436
摘 要：The effects of Yb2O3 particles on the microstructure and transport properties of YBa2Cu3O7-δ（YBCO） were investigated through resistance-temperature（R-T）,scanning electron microscope（SEM）,X-ray diffraction（XRD） and the critical current density（Jc） versus applied magnetic field（Jc-B） measurements.YBCO powder with Yb2O3 additives was synthesized using standard solid state reaction technique.Rietveld refinements of X-ray diffraction showed that both Yb2O3 and YBCO phases coexisted in the products.The critical current density（Jc） exhibited a maximum at x=0.05 in YBCO+xYb2O3 systems.Moreover,small additions of Yb2O3 in YBCO could enhance Jc by applying the magnetic field,although the superconducting temperature（Tc） decreased monotonically with increasing additive content.The characteristic behavior of Jc might come from the counterbalance of two effects simultaneously,which was caused by the inhomogeneity of grains distribution in nano-scale and degradation on superconducting properties.
徐胜1，虞爱平2，顾艳妮1，吴小山3
1. Jiangsu University of Science and Technology(Zhangjiagang Campus)2. Civil Engineering College,Guilin University of Technology3. Department of Physics,Nanjing University
摘 要：The effects of Yb2O3 particles on the microstructure and transport properties of YBa2Cu3O7-δ（YBCO） were investigated through resistance-temperature（R-T）,scanning electron microscope（SEM）,X-ray diffraction（XRD） and the critical current density（Jc） versus applied magnetic field（Jc-B） measurements.YBCO powder with Yb2O3 additives was synthesized using standard solid state reaction technique.Rietveld refinements of X-ray diffraction showed that both Yb2O3 and YBCO phases coexisted in the products.The critical current density（Jc） exhibited a maximum at x=0.05 in YBCO+xYb2O3 systems.Moreover,small additions of Yb2O3 in YBCO could enhance Jc by applying the magnetic field,although the superconducting temperature（Tc） decreased monotonically with increasing additive content.The characteristic behavior of Jc might come from the counterbalance of two effects simultaneously,which was caused by the inhomogeneity of grains distribution in nano-scale and degradation on superconducting properties.
关键词：