Cone-shaped cylindrical Ce0.9Gd0.1O1.95 electrolyte prepared by slip casting and its application to solid oxide fuel cells
来源期刊：Journal of Rare Earths2012年第1期
论文作者：隋静 董立峰 刘江
文章页码：53 - 56
摘 要：A cone-shaped gadolinium doped ceria（Ce0.9Gd0.1O1.95,GDC） electrolyte cylinder with a thin wall was fabricated using slip cast-ing technique.The diameter of the larger open end of the cone-shaped cylinder was 0.85 cm,the length was 1.0 cm,and the thickness of the wall was 0.026 cm after sintering.Both the electrolyte and electrode powders were fabricated by using a glycine-nitrate process.A single solid oxide fuel cell（SOFC） was prepared with the cone-shaped electrolyte,NiO-GDC（70:30 wt.%） anode and Sm0.5Sr0.5CoO3（SSC） cathode.Its electrochemical performance（I-V curve） and electrochemical impedance spectroscopy（EIS） were studied with humidified hydrogen as the fuel and air as the oxidant.The maximum output power density was about 300 ?mW/cm2 at 700 oC.The EIS results showed that the dominant loss of the SOFC was from the ohmic resistance of the electrolyte.
隋静1，董立峰1，刘江2
1. College of Materials Science and Engineering,Qingdao University of Science and Technology2. School of Chemistry and Chemical Engi-neering,South China University of Technology
摘 要：A cone-shaped gadolinium doped ceria（Ce0.9Gd0.1O1.95,GDC） electrolyte cylinder with a thin wall was fabricated using slip cast-ing technique.The diameter of the larger open end of the cone-shaped cylinder was 0.85 cm,the length was 1.0 cm,and the thickness of the wall was 0.026 cm after sintering.Both the electrolyte and electrode powders were fabricated by using a glycine-nitrate process.A single solid oxide fuel cell（SOFC） was prepared with the cone-shaped electrolyte,NiO-GDC（70:30 wt.%） anode and Sm0.5Sr0.5CoO3（SSC） cathode.Its electrochemical performance（I-V curve） and electrochemical impedance spectroscopy（EIS） were studied with humidified hydrogen as the fuel and air as the oxidant.The maximum output power density was about 300 ?mW/cm2 at 700 oC.The EIS results showed that the dominant loss of the SOFC was from the ohmic resistance of the electrolyte.
关键词：