Enhancement in energy product in Sm-Co/Fe exchange coupled magnetic layers with molybdenum interlayers
来源期刊：JOURNAL OF RARE EARTHS2010年第2期
论文作者：Furrukh Shahzad Saadat Anwar Siddiqi
文章页码：274 - 276
摘 要：Trilayers of Sm-Co/Mo/Fe were deposited by DC and RF magnetron sputtering on Si（100） substrate at 650 °C.Effect of very thin Mo interlayers on energy product of magnetic layers was studied.All the samples showed strong exchange coupling and single phase behavior.With increasing Mo interlayer thickness,we observed oscillating behavior of saturation magnetization and energy product.The rise in energy product was observed as 22% for 0.3 nm Mo interlayer as compared to sample without Mo interlayer.
Furrukh Shahzad1,2，Saadat Anwar Siddiqi1
1. Centre for Solid State Physics,University of the Punjab2. School of Physics and Microelectronics,Shandong University
摘 要：Trilayers of Sm-Co/Mo/Fe were deposited by DC and RF magnetron sputtering on Si（100） substrate at 650 °C.Effect of very thin Mo interlayers on energy product of magnetic layers was studied.All the samples showed strong exchange coupling and single phase behavior.With increasing Mo interlayer thickness,we observed oscillating behavior of saturation magnetization and energy product.The rise in energy product was observed as 22% for 0.3 nm Mo interlayer as compared to sample without Mo interlayer.
关键词：