简介概要

Microwave absorbing properties of NdFeCo magnetic powder

来源期刊:Journal of Rare Earths2012年第6期

论文作者:王磊 林培豪 潘顺康 周怀营

文章页码:529 - 533

摘    要:NdFeCo magnetic powder was prepared by the process of smelting,high-energy ball milling and oxidation heat treating.The effects of oxidation heat treatment and Co content on phase composition and microwave absorbing properties of NdFeCo magnetic powder were investigated by an X-ray diffractometer(XRD)and vector network analyzer.The minimum reflectivity of Nd23.25Fe36.75Co40 powder before oxidation heat treatment was-6.2 dB,and that of oxidized powder decreased to-14.0 dB.The microwave absorbing properties of NdFeCo magnetic powder could be improved effectively by oxidation heat treatment.With the increase of Co content,the Fe2O3 reduced and the Nd2O3 increased;Fe3Co7 phase appeared when the content of Co increased to 40%(mass ratio);the absorption peak was found to move towards lower frequency region first,and then it moved towards a higher frequency region.Nd23.25Fe66.75Co10 powder had better comprehensive properties in absorbing microwave in the frequency band of 3-13 GHz.The value of minimum reflectivity and absorption peak frequency,when the coating thickness(d)was 1.8 mm,were-19.7 dB and 4.8 GHz,respectively.

详情信息展示

Microwave absorbing properties of NdFeCo magnetic powder

王磊,林培豪,潘顺康,周怀营

Guangxi Key Laboratory of Information Materials,Guilin University of Electronic Technology

摘 要:NdFeCo magnetic powder was prepared by the process of smelting,high-energy ball milling and oxidation heat treating.The effects of oxidation heat treatment and Co content on phase composition and microwave absorbing properties of NdFeCo magnetic powder were investigated by an X-ray diffractometer(XRD)and vector network analyzer.The minimum reflectivity of Nd23.25Fe36.75Co40 powder before oxidation heat treatment was-6.2 dB,and that of oxidized powder decreased to-14.0 dB.The microwave absorbing properties of NdFeCo magnetic powder could be improved effectively by oxidation heat treatment.With the increase of Co content,the Fe2O3 reduced and the Nd2O3 increased;Fe3Co7 phase appeared when the content of Co increased to 40%(mass ratio);the absorption peak was found to move towards lower frequency region first,and then it moved towards a higher frequency region.Nd23.25Fe66.75Co10 powder had better comprehensive properties in absorbing microwave in the frequency band of 3-13 GHz.The value of minimum reflectivity and absorption peak frequency,when the coating thickness(d)was 1.8 mm,were-19.7 dB and 4.8 GHz,respectively.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号