Microstructure of hot-pack rolled Ti-43Al-9V-0.3Y alloy
来源期刊：中国有色金属学报(英文版)2003年第z1期
论文作者：CHEN Yu-yong(陈玉勇) KONG Fan-tao(孔凡涛) CHEN Zi-yong(陈子勇) TIAN Jing(田 竞)
文章页码：170 - 173
Key words：TiAl based alloys; rolling; rare earth; microstructure
Abstract: A kind of Ti-43Al-9V-0.3Y alloy sheet material using hot-pack rolling method is prepared. The microstructures of this alloy containing α2/γ lamellar microstructure, B2 phases and rare earth phases (YAl2) are investigated. The results show that the hot-rolled process can breakdown the as-cast structure, and a fine and homogeneous microstructure can be obtained after hot-rolling. The grains under the as-rolled condition are elongated in the rolling direction and flattened in the normal direction of the sheet. It is very likely that the mechanism for this change in grain size and shape is a grain boundary bulging of deformed grains rather than the nucleation and growth of new recrystallized grains. Subsequent heat treatment at 1260℃ for 1h and ageing at 1000℃ for 4h will lead to grain growth, and the average grain size of as-rolled Ti-43Al-9V-0.3Y alloy is about 100 μm after heat treatment.
CHEN Yu-yong(陈玉勇), KONG Fan-tao(孔凡涛), CHEN Zi-yong(陈子勇), TIAN Jing(田 竞)
(School of Materials Science and Engineering,
Harbin Institute of Technology, Harbin 150001, China)
Abstract:A kind of Ti-43Al-9V-0.3Y alloy sheet material using hot-pack rolling method is prepared. The microstructures of this alloy containing α2/γ lamellar microstructure, B2 phases and rare earth phases (YAl2) are investigated. The results show that the hot-rolled process can breakdown the as-cast structure, and a fine and homogeneous microstructure can be obtained after hot-rolling. The grains under the as-rolled condition are elongated in the rolling direction and flattened in the normal direction of the sheet. It is very likely that the mechanism for this change in grain size and shape is a grain boundary bulging of deformed grains rather than the nucleation and growth of new recrystallized grains. Subsequent heat treatment at 1260℃ for 1h and ageing at 1000℃ for 4h will lead to grain growth, and the average grain size of as-rolled Ti-43Al-9V-0.3Y alloy is about 100 μm after heat treatment.
Key words:TiAl based alloys; rolling; rare earth; microstructure