Improving Corrosion Resistance of Q235 Steel by Ni-Cr Alloyed Layer
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2012年第1期
论文作者：黄俊 张平则
文章页码：33 - 37
摘 要：Ni-Cr alloyed layer was formed on surface of Q235 steel by double glow plasma surface metallurgy to improve the corrosion resistance of substrate. The composition and microstructure of alloyed layer was analyzed by SEM and XRD. Potentiodynamic polarization and electrochemical impedance spectroscopy was applied to evaluate the corrosion resistance of the alloyed layer. The results showed working pressure had a great effect on structure of Ni-Cr alloyed layer, and the dense and smooth alloyed layer was prepared at 50 Pa working pressure. Compared with substrate, Ni-Cr alloyed layer exhibited higher corrosion potential, lower corrosion current density and larger charge transfer resistance, which indicated that Ni-Cr alloyed layer significantly modified the corrosion resistance of Q235 steel.
黄俊，张平则
College of Materials and Technology,Nanjing University of Aeronautics and Astronautics
摘 要：Ni-Cr alloyed layer was formed on surface of Q235 steel by double glow plasma surface metallurgy to improve the corrosion resistance of substrate. The composition and microstructure of alloyed layer was analyzed by SEM and XRD. Potentiodynamic polarization and electrochemical impedance spectroscopy was applied to evaluate the corrosion resistance of the alloyed layer. The results showed working pressure had a great effect on structure of Ni-Cr alloyed layer, and the dense and smooth alloyed layer was prepared at 50 Pa working pressure. Compared with substrate, Ni-Cr alloyed layer exhibited higher corrosion potential, lower corrosion current density and larger charge transfer resistance, which indicated that Ni-Cr alloyed layer significantly modified the corrosion resistance of Q235 steel.
关键词：