Effect of Ni on Sintering Characteristics of Short Cast Iron Fibre
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG1992年第6期
论文作者：李东春 田永君 陈世镇 于栋利 何巨龙
文章页码：417 - 420
摘 要：<正> Nickel,as the carrier through which Fe atomsdiffuse,obviously enhances the densification ofsintered compact containing short cast iron fibre.When Ni content is above 4.5 wt-% there are someaustenites in microstructure at room temperature,discontinuous cementite networks at the interfacesbetween austenites and pearlites,free graphite pre-cipitated in austenite and pores andWidmannst（?）tten carbide precipitated in austenite.When Ni content is about 12 wt-%,it leads to de-crease in densification ratio and change in fracturemorphology of sintered compact from ductile tobrittle.
李东春，田永君，陈世镇，于栋利，何巨龙
摘 要：<正> Nickel,as the carrier through which Fe atomsdiffuse,obviously enhances the densification ofsintered compact containing short cast iron fibre.When Ni content is above 4.5 wt-% there are someaustenites in microstructure at room temperature,discontinuous cementite networks at the interfacesbetween austenites and pearlites,free graphite pre-cipitated in austenite and pores andWidmannst（?）tten carbide precipitated in austenite.When Ni content is about 12 wt-%,it leads to de-crease in densification ratio and change in fracturemorphology of sintered compact from ductile tobrittle.
关键词：