Performance of Concrete Subjected to Severe Multiple Actions of Composite Salts Solution under Wet-Dry Cycles and Flexural Loading in Lab
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第4期
论文作者：陈燕娟 高建明 TANG Luping SHEN Daman
文章页码：830 - 837
摘 要：Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity（Erd values） were monitored, as well as the key factor impacting on the chloride ingress when concrete subjected to multiple action regimes was identified by the method of Grey Relation Analysis（GRA）. The changes in micro-structures and mineral products of interior concrete after different action regimes were investigated by means of X-ray diffraction（XRD）, mercury intrusion technique（MIP）, and scanning electron microscopy（SEM）. The test results showed that the cyclic wet-dry accelerated the deterioration of OPC concrete more than the action of 35% flexural loading based on the results of Erd values and the GEA. The analyses from micro-structures could give certain explanations to the change in Erd values under different action regimes.
陈燕娟1,2，高建明1,2，TANG Luping3，SHEN Daman1,2
1. Department of Materials Science and Engineering, Southeast University2. Key Laboratory of Construction Materials, Southeast University3. Chalmers University of Technology
摘 要：Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity（Erd values） were monitored, as well as the key factor impacting on the chloride ingress when concrete subjected to multiple action regimes was identified by the method of Grey Relation Analysis（GRA）. The changes in micro-structures and mineral products of interior concrete after different action regimes were investigated by means of X-ray diffraction（XRD）, mercury intrusion technique（MIP）, and scanning electron microscopy（SEM）. The test results showed that the cyclic wet-dry accelerated the deterioration of OPC concrete more than the action of 35% flexural loading based on the results of Erd values and the GEA. The analyses from micro-structures could give certain explanations to the change in Erd values under different action regimes.